A use could be found for pulsed-plasma nitrided AISI 316L stainless steel in a wide range of biomedical applications, e.g. femoral and biarticular heads of joint prostheses. Forged samples of steel were pulsed-plasma nitrided at a temperature of 540°C for 24 hours to increase the hardness of the surface. During nitriding, the hardness of the ?$70 \mu$? nitride layer uniformly increased to 958 HV 0.1. The hardness of steel below the nitride layer remained unchanged, 210 HV 0.1. The thickness of the layer depended on the process parameters. The research showed that nitriding of stainless steel for medical implants in pulsed plasma is feasible.

Rights

URN

URN:NBN:SI:doc-XMPH7SRN

COBISS ID

19114

Added

22.07.2011

Metadata

Citation

APA:

Torkar, Matjaž, Leskovšek, Vojteh, Rjazancev, B. (1995). Pulsed plasma nitriding of stainless steel, volume 29, issue 3/4. URN:NBN:SI:doc-XMPH7SRN from http://www.dlib.si

MLA:

Torkar, Matjaž, Leskovšek, Vojteh, Rjazancev, B.. Pulsed plasma nitriding of stainless steel. Inštitut za kovinske materiale in tehnologije
Železarna Jesenice
Železarna Ravne
Železarna Štore, 1995.
<http://www.dlib.si/?URN=URN:NBN:SI:doc-XMPH7SRN>

Kovine zlitine tehnologije
1992-1999
(Assembly record)

prejšnja

Hydrogen and temper embrittlement of medium strength steel
1995
(Previous issue)

naslednja

Razvoj visokovakuumske oljne difuzijske frakcionirne črpalke s premerom sesalne odprtine 650 mm
1995
(Next issue)

Pulsed plasma nitriding of stainless steelNitriranje nerjavnega jekla v pulzirajoči plazmi

Pulsed plasma nitriding of stainless steel
Nitriranje nerjavnega jekla v pulzirajoči plazmi