10 KB597 KB9 KB199219991995Leskovšek, VojtehRjazancev, B.Torkar, Matjažletnik:29številka:3/44 stranistr. 413-416ISSN:1318-0010COBISSID:19114URN:URN:NBN:SI:doc-XMPH7SRNenInštitut za kovinske materiale in tehnologijeŽelezarna JeseniceŽelezarna RavneŽelezarna ŠtoreKovine zlitine tehnologijebiomedicinajeklonerjavno jeklonitriranjePulsed plasma nitriding of stainless steel| Nitriranje nerjavnega jekla v pulzirajoči plazmi|A use could be found for pulsed-plasma nitrided AISI 316L stainless steel in a wide range of biomedical applications, e.g. femoral and biarticular heads of joint prostheses. Forged samples of steel were pulsed-plasma nitrided at a temperature of 540°C for 24 hours to increase the hardness of the surface. During nitriding, the hardness of the ?$70 \mu$? nitride layer uniformly increased to 958 HV 0.1. The hardness of steel below the nitride layer remained unchanged, 210 HV 0.1. The thickness of the layer depended on the process parameters. The research showed that nitriding of stainless steel for medical implants in pulsed plasma is feasibleNerjavno jeklo AISI 316L, nitrirano v pulzirajoči plazmi, bi bilo mogoče uporabiti za biomedicinske namene, npr. za femoralne in biartikularne glave kolčnih vsadkov. Kovani vzorci jekla so bili nitrirani v pulzirajoči plazmi 24 ur na temperaturi 540°C. Med nitriranjem je trdota ?$70 \mu$? debele plasti enakomerno narasla do 958 HV 0.1. Trdota jekla pod nitrirano plastjo je ostala nespremenjena, 210 HV 0.1. Debelina nitrirane plasti je odvisna od parametrov procesa. Raziskava je pokazala, da je nitriranje medicinskih implantatov v pulzirajoči plazmi izvedljivoTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije