The capacibilities of establishing mutual electrical insulation between particles of amorphous ?Fe_{40{Ni_{40}Si_{14}B_6$? and of microcristaline 8ONiFe alloys were investigated. Their surface was oxidated in alkaline solution of ?$KMnO_4$? and phosphatated by ?$H_3PO_4$?. The highest breakdown voltages were achieved at 8ONiFe alloy oxidation. They are comparable to breakdown voltages at isolated carbonyl powders. For the ?$Fe_{40}Ni_{40}Si_{14}B_6$? alloy substantially lower breakdown voltages were significant.

Rights

URN

URN:NBN:SI:doc-RMAJFSQD

COBISS ID

18176005

Added

22.07.2011

Metadata

Citation

APA:

Brecelj, Franc, Zupan, Klementina (1995). Električna izolacija amorfnih Fe-Ni prahov, volume 29, issue 1/2. URN:NBN:SI:doc-RMAJFSQD from http://www.dlib.si

MLA:

Brecelj, Franc, Zupan, Klementina. Električna izolacija amorfnih Fe-Ni prahov. Inštitut za kovinske materiale in tehnologije
Železarna Jesenice
Železarna Ravne
Železarna Štore, 1995.
<http://www.dlib.si/?URN=URN:NBN:SI:doc-RMAJFSQD>

Kovine zlitine tehnologije
1992-1999
(Assembly record)

prejšnja

Izboljšanje mehanskih lastnosti spajkanih spojev s kompozitno spajko
1995
(Previous issue)

naslednja

Razširjene perspektive navarjanja močno legiranih nanosov
1995
(Next issue)