9 KB367 KB9 KB199219991995Brecelj, FrancZupan, Klementinaštevilka:1/2letnik:293 stranistr. 319-321ISSN:1318-0010COBISSID:18176005URN:URN:NBN:SI:doc-RMAJFSQDslInštitut za kovinske materiale in tehnologijeŽelezarna JeseniceŽelezarna RavneŽelezarna ŠtoreKovine zlitine tehnologijeelektrična izolacijaizolacijska trdnostkovinska steklaElektrična izolacija amorfnih Fe-Ni prahov|The capacibilities of establishing mutual electrical insulation between particles of amorphous ?Fe_{40{Ni_{40}Si_{14}B_6$? and of microcristaline 8ONiFe alloys were investigated. Their surface was oxidated in alkaline solution of ?$KMnO_4$? and phosphatated by ?$H_3PO_4$?. The highest breakdown voltages were achieved at 8ONiFe alloy oxidation. They are comparable to breakdown voltages at isolated carbonyl powders. For the ?$Fe_{40}Ni_{40}Si_{14}B_6$? alloy substantially lower breakdown voltages were significantRaziskovali smo možnosti medsebojne električne izolacije prašnih zrnc amorfnih in mikrokristaliničnih zlitin 8ONiFe in ?$Fe_{40}Ni_{40}Si_{14}B_6$?. Površino zrnc smo oksidirali v alkalni raztopini ?$KMnO_4$? in fosfatirali s ?$H_3PO_4$?. Najvišje prebojne napetosti so bile dosežene pri površinski oksidaciji zlitine 8ONiFe in so primerljive s temi napetostmi pri izoliranem karbonilnem železu. Občutno nižje prebojne napetosti so bile karakteristične za zlitino ?Fe_{40}Ni_{40}Si_{14}B_6$?TEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije