The strength of the vacuum brazing joint between cemented carbide particles and the structural steel base depends on microstructural characteristics of the hard metal/braze interface formed during vacuum razing. These are determined by the selected brazing agent, the structural steel base, as well as the vacuum brazing procedure. R&D work concerning the procedure of manufacturing these types of grinding tools is introduced, with a strong emphasis on the characteristics of the brazing agent used, the vacuum brazing procedure, as well as the resulting microstructural characteristics of the brazing joint between the hard metal particles and the structural steel base.

Rights

URN

URN:NBN:SI:doc-L7YQT2J5

COBISS ID

7082

Added

22.07.2011

Metadata

Citation

APA:

Šuštaršič, Borivoj, Leskovšek, Vojteh, Rodič, Alenka (1995). Characteristics of cemented carbide particles/structural steel vacuum brazing joint, volume 29, issue 3/4. URN:NBN:SI:doc-L7YQT2J5 from http://www.dlib.si

MLA:

Šuštaršič, Borivoj, Leskovšek, Vojteh, Rodič, Alenka. Characteristics of cemented carbide particles/structural steel vacuum brazing joint. Inštitut za kovinske materiale in tehnologije
Železarna Jesenice
Železarna Ravne
Železarna Štore, 1995.
<http://www.dlib.si/?URN=URN:NBN:SI:doc-L7YQT2J5>

Kovine zlitine tehnologije
1992-1999
(Assembly record)

prejšnja

Razvoj visokovakuumske oljne difuzijske frakcionirne črpalke s premerom sesalne odprtine 650 mm
1995
(Previous issue)

naslednja

Influence of fracture toughness on vacuum hardened HSS
1995
(Next issue)

Characteristics of cemented carbide particles/structural steel vacuum brazing jointZnačilnosti vakuumskega spoja zrn karbidne trdine s konstrukcijskim jeklom

Characteristics of cemented carbide particles/structural steel vacuum brazing joint
Značilnosti vakuumskega spoja zrn karbidne trdine s konstrukcijskim jeklom