The CTOD values measured on 34 mm thick SENB specimen taken from multipass 1/2K joints were compared with the values obtained from 8 mm thick SENB specimens with simulated microstructures of CGHAZ (a/W=0.5). Single and double thermal cycles were used to simulate various thermal treatment which HAZ at the weld bond may xperience during the welding.

Rights

URN

URN:NBN:SI:DOC-TD898JAQ

COBISS ID

2463766

Added

22.07.2011

Metadata

Citation

APA:

Rak, Inoslav, Koçak, Mustafa, Petrovski, B., Gliha, Vladimir (1995). HAZ toughness of Ti-microalloyed ofshore steel in as-welded and simulated condition, volume 29, issue 5/6. URN:NBN:SI:DOC-TD898JAQ from http://www.dlib.si

MLA:

Rak, Inoslav, Koçak, Mustafa, Petrovski, B., Gliha, Vladimir. HAZ toughness of Ti-microalloyed ofshore steel in as-welded and simulated condition. Inštitut za kovinske materiale in tehnologije
Železarna Jesenice
Železarna Ravne
Železarna Štore, 1995.
<http://www.dlib.si/?URN=URN:NBN:SI:DOC-TD898JAQ>

Kovine zlitine tehnologije
1992-1999
(Assembly record)

prejšnja

Operational aspects of experiences in vacuum technology by production of high quality stainless and alloyed steels
1995
(Previous issue)

naslednja

Difuzija železovih ionov v kromitno magnezitnih gradivih
1995
(Next issue)

HAZ toughness of Ti-microalloyed ofshore steel in as-welded and simulated conditionHAZ žilavost mikrolegiranih Ti-ofshore jekel v varjenem in simuliranem stanju

HAZ toughness of Ti-microalloyed ofshore steel in as-welded and simulated condition
HAZ žilavost mikrolegiranih Ti-ofshore jekel v varjenem in simuliranem stanju