D. STEINER PETROVI^, R. [TURM: SENSITIVITY OF WECK’S REAGENT TO THE MICROSTRUCTURE INHOMOGENEITIES ... 687–693 SENSITIVITY OF WECK’S REAGENT TO THE MICROSTRUCTURE INHOMOGENEITIES OF A PULSE-LASER-MODIFIED AlSi12CuNiMg ALLOY OB^UTLJIVOST WECKOVEGA REAGENTA NA MIKROSTRUKTURNE NEHOMOGENOSTI S PULZNIM LASERJEM MODIFICIRANE ZLITINE AlSi12CuNiMg Darja Steiner Petrovi~ 1 , Roman [turm 2 1 Institute of Metals and Technology, Lepi pot 11, 1000 Ljubljana, Slovenia 2 University of Ljubljana, Faculty of Mechanical Engineering, A{ker~eva 6, 1000 Ljubljana, Slovenia darja.steiner@imt.si Prejem rokopisa – received: 2018-04-26; sprejem za objavo – accepted for publication: 2018-05-18 doi:10.17222/mit.2018.087 In order to optimize laser cladding using pulsed-laser procedures, in particular to prevent failures of the cladding, a systematic ex-situ characterization can provide a lot of valuable information about the effects of the process parameters on the resulting microstructure and hardness. In this study, a TiC/TiB2 cladded layer was produced by laser scanning over a pre-placed TiC/TiB2/Al powder mixture on an aluminum alloy using a Nd:YAG pulsed laser. The increasing of the EEDV (effective energy density per volume) influences larger scattering of the cladded-layer thickness, whereas the decreasing of the EEDV influences the decrease of its surface roughness. The average hardness of the 0.1-mm-thick layer was 400±10 HV 0.3, which confirmed an improvement in the mechanical properties of the surface. The microstructures were investigated using FE-SEM/EDS and light microscopy. An additional color chemical etching using Weck’s reagent at room temperature was performed. Using color etching, the laser-affected features, i.e., the penetration depth, the melt pool, its boundaries and various inhomogeneities, could be clearly distinguished. The sensitivity of the color etchant to the morphological and compositional differences was confirmed by FE-SEM/EDS analyses and microhardness measurements. Keywords: aluminum, pulse laser, cladding, morphological inhomogeneity, Weck’s reagent Z namenom prepre~evanja nastanka napak pri optimiranju laserskih postopkov oblaganja s pulznim laserjem nam sistemati~na ex-situ karakterizacija lahko nudi veliko dragocenih informacij o vplivu procesnih parametrov na razvoj mikrostrukture in trdote. V tej raziskavi smo na aluminijevo zlitino s pomo~jo laserskega pretaljevanja prednane{ene me{anice prahu TiC/TiB2/Al naredili oblogo TiC/TiB2. V postopku smo uporabili pulzni laser Nd:YAG. Pove~evanje EEDV (efektivne gostote energije na enoto volumna) vpliva na ve~ji raztros debelin oblo`enega sloja, zmanj{evanje EEDV pa vpliva na zmanj{anje hrapavosti povr{ine. Povpre~na trdota 0,1 mm debelega oblo`enega sloja je 400±10 HV 0,3, kar potrjuje izbolj{anje mehanskih lastnosti povr{ine. Mikrostrukture smo preu~evali z uporabo tehnik FE-SEM/EDS in svetlobno mikroskopijo. Pri sobni temperaturi smo izvedli dodatno barvno kemijsko jedkanje z Weckovim reagentom. Z uporabo barvnega jedkanja lahko razkrijemo {tevilne ne- homogenosti, ki so posledica vpliva laserske obdelave, npr. globino penetracije, bazen taline, njegove robove... Ob~utljivost barvnega jedkala na morfolo{ke razlike smo potrdili z analizami FE-SEM/EDS in meritvami mikrotrdote. Klju~ne besede: aluminij, pulzni laser, oblaganje, morfolo{ke nehomogenosti, Weckov reagent 1 INTRODUCTION When aluminum alloys are to be used for specific applications where a high hardness, special strength, good wear resistance, etc., are needed, an additional surface protection of the alloys is essential. For several decades laser surface engineering (LSE) has been used for a wide range of applications in order to modify and improve the microstructure and properties of metallic materials in a highly controllable way. 1–9 In one of the techniques of LSE, the laser cladding is verified as being an effective and economical method for the in-situ synthesis of advanced coating materials with a rapidly solidified, refined microstructure and the production of advanced coatings. 2,10–13 To increase the hardness of the surface layer of alu- minum alloys a laser cladding with a ceramic mixture of TiC and TiB 2 can be applied. 14–19 The average micro- hardness of TiC and/or TiB 2 coatings is higher than the substrate’s hardness, and the coatings show a better wear resistance. 2,15–18 For a higher content of TiB 2 in the ceramic components, the flexural strength of the coated aluminum specimens is increased, thus delaying the occurrence of the first crack in the coating or the occurrence of delamination. 17 Furthermore, the corrosion resistance of the laser-cladded specimens is better than the substrate. 18 It was reported that chemical reactions between TiB 2 and liquid aluminum have not been ob- served during the process of laser cladding. The obtained microstructure showed TiB 2 dispersed in -Al dendrites and an -Al+Si eutectic. 15 On the other hand, a small proportion of TiC dissolves in the melt, resulting in a mi- crostructure composed of TiC and Ti 3 SiC 2 particles Materiali in tehnologije / Materials and technology 52 (2018) 6, 687–693 687 UDK 620.1:67.017:620.192.3:669.017.15 ISSN 1580-2949 Original scientific article/Izvirni znanstveni ~lanek MTAEC9, 52(6)687(2018) dispersed in a matrix consisting of pro-eutectic -Al dendrites and an -Al+Si eutectic. 16 The cladding process depends on several experi- mental parameters that must be optimized to generate tracks of high quality. Therefore, the characterization of the produced clads is essential for process control. In the characterization of coatings produced using the laser- cladding technique, laser-induced breakdown spectro- scopy (LIBS) has been proven to be a suitable tool, especially for materials that exhibit an inhomogeneous distribution of elements. 12 If an optimal clad layer (well-bonded, thick, dense and without cracks) is to be formed, the laser single- tracks’ geometrical characteristics, such as width, height, penetration depth, dilution and wetting angle, should be identified. As a guide, a laser-cladding processing map can be drawn. 13 However, the visual determination of various in- homogeneities in laser-cladded and/or melted micro- structures, e.g., compositional gradients and changes, is of great importance for producing more uniform clads, but this can be very challenging. In the scientific litera- ture, there is no reference that reports the use of Weck’s reagent as a color etchant for laser-surface-modified aluminum alloys. Therefore, the objectives of the present work are two-fold: (i) to investigate the effect of the pulsed laser’s peak power density on the characteristics of the TiC/TiB 2 laser cladding and (ii) to evaluate the sensitivity of Weck’s reagent to the microstructure inhomogeneities of the laser-modified AlSi12CuNiMg alloy, and to show that relevant information about the resulting microstructure can be obtained through the use of color etching. 2 MATERIALS AND METHODS 2.1 Cladding powders and substrate alloy The cladding material was a mixture of TiC, TiB 2 and Al powders (60 w/%, 20 w/%, 20 w/%, respectively). Due to the differences in the melting points of the TiC, TiB 2 and the aluminum alloy, Al powder was added to achieve better bonding between the cladded layer and the substrate. 17 The diameters of the powder particles were between 4 μm and 8 μm. The chemical composition of the selected substrate, a hypo-eutectic aluminum alloy AlSi12CuNiMg (EN AC 48000), is given in Table 1. Table 1: Chemical composition of Al alloy substrate (w/%). Si Mg Cu Ni Ti Al 12 1.04 0.93 0.9 0.01 Balance The microstructure of the AlSi12CuNiMg alloy is composed of primary dendrites of -Al with an inter- dendritic network of -Al-Si eutectic. The thermodyna- mic calculations (TDC) of the stability of the equilibrium phases in the aluminum alloy were performed using the ThermoCalc, TTAl7 database. As confirmed by the TDC, various intermetallic compounds, e.g., Al 3 Ti, Al 3 Ni, Al 7 Cu 4 Ni and Al 5 Cu 2 Mg 8 Si 6 , are stable under equilibrium solidification conditions at room tempe- rature. The aluminum alloy was used in the as-delivered state, i.e., in the as-cast state with an additional homo- genization heat treatment. The heat treatment involves hardening to maximum strength using a solution heat treatment at 520–530 °C for 5–10 h, followed by quenching and artificial ageing at 150–175 °C for 15–5 h. The obtained mechanical properties of the substrate are given in Table 2. Table 2: Mechanical properties of Al substrate Hardness HV 0.3 Tensile strength R m/MPa Yield strength R p0.2 /MPa Elongation A 5/% 120±1 280 240 1 The dimensions of the aluminum-alloy substrates prepared for the laser cladding were (65 × 20 × 2.5) mm. The specimen surface was ground using 800-grit emery paper prior to applying the cladding mixture to the surface in order to eliminate the existence of the thick oxides. A thin layer of pre-paste powder mixture (with an approximate thickness of h = 0.15 mm) was applied to the substrate surface with an air gun. For better adhesion of the powders to the substrate surface, the cladding powders were mixed with alcohol to form a wet paste. 2.2 Laser surface cladding An approach using a pulsed, low-power Nd:YAG laser was chosen to investigate the suitability of this technique for the surface cladding. The procedures using a pulsed Nd:YAG laser could act as a cost-effective tool for advanced surface engineering or when an effective repair procedure for the damaged surface during its exploitation is needed, or both. 6,19 The laser surface cladding was performed on speci- mens using an OR Laser, type: ECO BU80 Nd:YAG laser, with a maximum mean power of 80 W and a D. STEINER PETROVI^, R. [TURM: SENSITIVITY OF WECK’S REAGENT TO THE MICROSTRUCTURE INHOMOGENEITIES ... 688 Materiali in tehnologije / Materials and technology 52 (2018) 6, 687–693 Figure 1: Laser treatment on the substrate top-hat mode structure, using the following experimental parameters: • Average pulse power: P a = 46.5 W • Wavelength: = 1064 nm • Frequency of pulse: f=7Hz • Pulse duration: t p =8ms • Maximum pulse power: P p = 0.83 kW • Pulse energy: E p = 6.64 J For this study, a combination of pulse duration and pulse frequency was chosen in such a way that the average power did not reach the limit of the Nd:YAG laser system used. A protective argon gas of 99.995 % purity and a flow rate of 5 l/min was used during the whole process to minimize the surface oxidation. In our experiment we were changing the laser beam’s travelling speed on the specimen’s surface. The laser beam changed its movement at a distance of 0.7 mm, as shown in Figure 1. The laser beam’s parameters were: • Beam travel speed: v b = 100, 150, 200 mm/min • Beam diameter on the specimen surface: D b = 1.0 mm. As described elsewhere 19 the following laser-pro- cessing characteristics can be calculated: • Laser path overlapping: O p =30%, where: O Dx D p b b = − ⋅ Δ 100% (1) • Overlapping factor between laser pulses: O f = 54, 65 and 77 %, where: ODvt v f vf Dvt fbb p b b bb p =+⋅− ⎛ ⎝ ⎜ ⎞ ⎠ ⎟ ⎡ ⎣ ⎢ ⎤ ⎦ ⎥⋅= =− +⋅ ()% / 100 1 ⎛ ⎝ ⎜ ⎞ ⎠ ⎟ ⋅100% (2) Due to the nature of the pulsed beam, an effective energy density (EED) was calculated to determine the total energy input during the laser processing: 19 EED EF A = ⋅ p (J/mm 2 ) (3) where A (mm 2 ) is the area of laser spot on the specimen, F is the cumulative overlapping index defined as: Fn nv fD =+⋅− +⋅ ⋅ ⎡ ⎣ ⎢ ⎤ ⎦ ⎥ 11 1 2 () b b (4) n Df v = ⋅ b b (5) In a laser-cladding process the effective energy density per volume (EEDV) of the pre-pasted powder is a more appropriate parameter for evaluating the results: 20, 21 EEDV EED h = (J/mm 3 ) (6) The calculated EEDV is, according to different EED and h, in the range between 87 J/mm 3 and 146 J/mm 3 . 2.3 Metallography and chemical etching For the metallographic analyses the specimens were ground and polished in accordance with standard metallographic techniques. The metallographic analyses were performed using light microscopy and scanning electron microscopy. The field-emission scanning elec- tron microscope was a JEOL JSM 6500-F equipped with an energy-dispersive spectrometer. The FE-SEM/EDS analyses were performed at a 10-kV accelerating volt- age. For the light microscopy we used a Nikon Micro- phot FXA microscope. No additional filters or analyzers were used. In order to reveal the solidification microstructure Weck’s reagent (i.e.,4gofKMnO 4 ,1gofNaOH and 100 ml of distilled water) was used for the chemical etching. The etching was performed at room temperature for 10 s. 2.4 Hardness and surface roughness The hardnesses of the clad layer and the base material were measured using a load of 300 g (HV 0.3) on metallographically polished cross-sections of the laser-cladded specimens. In addition, microhardness measurements were performed separately in the laser- affected areas using a load of 50 g (HV 0.05). The Vickers microhardness was measured using an Instron Wilson-Wolpert Tukon 2100B hardness tester. The measurements were performed in accordance with the Vickers method, i.e., a diamond-pyramid hardness measurement, through the depth of the alloyed layer. The dwell time of the test load was 12 s. The surface roughness (R a ) was measured using a profilometer Surtronic 3+/TalyProfile Lite 3.1.4.,+, Taylor-Hobson, with a sampling length of 8 mm and a measurement speed of 0.5 mm/s. Five measurements on each sample were performed. 3 RESULTS AND DISCUSSION The pulsed Nd:YAG laser, typically used for such welding, was chosen to investigate the suitability of this technique for the surface modification via laser surface cladding. In order to prevent various failures of the cladded coating, and for the optimization of the laser- based procedures, the identification of the penetration depth and the dilution zone is valuable information. To reveal the laser-affected, sub-surface areas of the aluminum alloy more clearly, a systematic metallo- graphic characterization was performed. Additionally, color chemical etching using Weck’s reagent was per- formed. D. STEINER PETROVI^, R. [TURM: SENSITIVITY OF WECK’S REAGENT TO THE MICROSTRUCTURE INHOMOGENEITIES ... Materiali in tehnologije / Materials and technology 52 (2018) 6, 687–693 689 3.1 Laser-cladded layer By varying the selected parameter, i.e., the effective energy density per volume (EEDV) of pre-pasted powder = (87, 107, and 146) J/mm 3 , the laser-surface cladding of the aluminum alloy with the TiC+TiB 2 +Al powder pro- duced a characteristic microstructure, as shown in Figure 2. Under different applied conditions, the thicknesses of the obtained TiC/TiB 2 layer were in the range from 0.03 mm to 0.15 mm. The average thickness of the laser-cladded layer is around 0.1 mm. The average hard- ness of the approximately 0.1-mm-thick TiC/TiB 2 laser- clad layer is 400±10 HV 0.3. The average thickness of the melted aluminum beneath the laser-cladded layer is around 0.15 mm, in the range between 0.05 mm and 0.22 mm. Table 3 presents the correlation between v b , O f , EEDV, and the thickness and roughness of the laser- cladded surface. Taking into account the influence of laser beam’s movement (see Figure 1) we can also ob- serve a larger scattering of cladded-layer dimensions with the increasing of the EEDV, whereas the decreasing of the EEDV influences the decrease of the surface roughness R a of the cladded surface. Table 3: Laser-cladding parameters and dimensions of the cladded surface v b (mm/min) O f (%) EEDV (J/mm 3 ) Cladded layer thick- ness d (μm) Surface roughness R a (μm) 100 77 146 35–104 11–17 150 65 107 50–95 6–7 200 54 87 111–145 3–5 3.2 Metallographic analyses The produced clad layers are predominantly dense and thick. A typical microstructure of a laser-cladded TiC/TiB 2 layer on an aluminum specimen is shown in Figure 2. In the micrograph presented in Figure 2a well-bound, laser-clad layer of TiC/TiB 2 on an AlSi12CuNiMg substrate can be seen. In the clad layer, the powder is well mixed with the base material, or vice versa, the powder is incorporated into the remelted layer. Using the pulsed-laser processing parameters, some discontinuities were revealed, depending on the sample’s geometry. This was particularly significant in the laser-modified areas lying at the sample’s edges. In Figure 3a a discontinuity section is shown. Due to the fact that the area is near the sample’s edge, the selected laser parameters produced different effects than on the bulk substrate (Figure 2). Through the selected cross-section, the chemical composition of the sample is very nonhomogeneous. Microchemical EDS analyses revealed the presence of Ti, B, and C on the surface clad-region and in some subsurface areas (Table 4). As can be seen in Figure 3a, an exact determination of the laser-affected zones is very challenging. Therefore, a color chemical etching using Weck’s reagent was applied (Figure 3b). A colored microstructure with an enlarged section of the discontinuity section of the laser-clad layer before and after color etching are presented in Figure 4. The microstructures of the laser-treated materials that form during the re-solidification critically determine the properties. Microstructure variations in the subsurface laser-melted and affected Al-alloy substrate from Fig- D. STEINER PETROVI^, R. [TURM: SENSITIVITY OF WECK’S REAGENT TO THE MICROSTRUCTURE INHOMOGENEITIES ... 690 Materiali in tehnologije / Materials and technology 52 (2018) 6, 687–693 Figure 3: a) FE-SEM/EDS analyses of laser-modified Al alloy, non-etched, b) Microstructure after chemical etching using Weck’s reagent (LM). Areas of microhardness measurements are designated. EEDV = 107 J/mm 3 , c) X-ray map of Si in FE-SEM region of interest Figure 2: Laser-clad layer of TiC/TiB 2 on substrate. EEDV =1 0 7 J/mm 3 ure 3b also result in different colors and Vickers micro- hardnesses. They are listed in Table 5. Table 4: EDS analyses of the selected points and areas from Figure 3a Spec- trum BCOM gA lS iT iC u 1 37.65 3.11 – – 0.53 – 58.71 – 2 36.86 3.09 – – 0.37 – 59.68 – 3 34.44 – – – 0.31 – 65.24 – 4 – 2.08 – 1.31 82.20 13.62 – 0.79 5 – 1.65 0.91 1.37 86.20 8.63 – 1.24 6 – – 0.96 – 63.24 35.04 – 0.77 7 – – 0.67 0.41 96.55 1.77 – 0.60 8 36.07 3.30 – – 0.23 – 60.40 – 9 32.60 10.83 3.26 – 23.49 1.32 28.50 – Table 5: Vickers microhardness of the designated areas from Figure 3b Area Microhardness Si (w/%) Color 1 210 HV 0.05 / Red-brown 2 185 HV 0.05 13.62 Marine-blue 3 183 HV 0.05 / Violet 4 163 HV 0.05 / Light Violet 5 135 HV 0.05 35.04 Light Blue 6* 120 HV 0.3 8.63 White – Light Violet *Matrix, not affected by laser. Out of site of Figure 4b The softest part of the analyzed microstructure is the base material that is not affected by the laser surface treatment (120 HV 0.3). Here, a slightly harder micro- structure component is at site 5 in Figure 3b, where a remarkable silicon segregation was detected (see Table 4 – Spectrum 6). On the other hand, the semi-hemispheri- cally created melt pool is much harder. Due to the moving heat source, the hardness depends on the local solidification parameters. High thermal gradients occurr- ing during the laser pulses with a high power density lead to fine distributed and hard structures. 5 The micro- hardnesses range from 185 to 210 HV 0.05, and that of the dilution zone is about 165 HV 0.05. The effects of color etching shown in Figure 3b and 4b were also compared with the FE-SEM/EDS micro- analyses of the polished sample. Surprisingly, a compa- rison of the EDS analyses, the X-ray map of Si and the color-etched images (Figure 3a to 3c) reveal that the bluish-colored parts of the microstructure might contain more Si. Using a comparison between the microchemical analyses of the selected points the silicon segregations are detected in the laser-melted area as well as in the base material, as seen from Figure 3a, Table 4, spectra 4 and 6, and Figure 3b, site 5. Similar to cast iron, 22 the bluish colors represent a higher Si content in the laser- affected aluminum. It can be seen that the laser-affected areas, i.e., the melt pool and its boundaries, can be better distinguished when using color etching. Moreover, the morphological texture of the previously scanned neighboring tracks 5 in the evolved microstructure can be followed. Selective color etching is more sensitive to morphological diffe- rences and compositional gradients; therefore, the accuracy of the metallographic analysis compared to the gray-scale etchings can be improved. 22 After applying the chemical etching with Weck’s reagent the melting pool, the penetration depth as well as various microstructure inhomogeneities are selectively tinted (Figure 4b). The penetration depth was about 0.250 mm. The microstructure of the penetration zone can be roughly D. STEINER PETROVI^, R. [TURM: SENSITIVITY OF WECK’S REAGENT TO THE MICROSTRUCTURE INHOMOGENEITIES ... Materiali in tehnologije / Materials and technology 52 (2018) 6, 687–693 691 Figure 4: a) An enlarged section of the discontinuity section of a laser-clad layer before etching, b) after color etching. EEDV = 107 J/mm 3 . divided into the following areas: area of the dilution substrate, melted substrate, and heat-affected zone bet- ween the penetration zone and the substrate. 23 The color differences in the surrounding regions of the melt pool can be ascribed to the micro-segregation-sensitive nature of Weck’s reagent. 24,25 Outside the melt pool, the den- dritic nature of the initial microstructure is seen. The shape of the melt pool is determined using three different isotherms: a) the liquidus temperature of the substrate material ahead of the laser beam, as the substrate has to be melted to ensure a metallurgical bond; b) the liquidus temperature of the coating material; and c) the solidus temperature of the coating material. 26 The color etchants are reagents that remove a thin layer from the surface of the specimen and simultaneously dissolve it, leaving a thin film on the surface. 20 In the case of aluminum alloys the growth of the film is strongly influenced by the so- lute micro-segregations. The addition of different solutes can also affect the surface chemical reactions and, there- fore, the colors change as a result. 24,25 Since Al and various alloying elements as well as the selected cladd- ing powders have significant differences in their che- mical and physical properties, the interface region and the laser-melted regions display an inhomogeneous composition that is consistent with previous scientific reports by Wang et al. 10,11 Color etching is very well suited to characterizing laser-surface-modified aluminum specimens. It can be recommended as a valuable step in the metallographic analysis of laser-melted aluminum specimens. 4 CONCLUSIONS An AlSi12CuNiMg alloy substrate was surface modified using pulsed-laser cladding with a ceramics mixture of TiC/TiB 2 /Al to increase the hardness of the surface layer. The effect of the pulsed laser’s effective energy density per volume of pre-pasted powder, i.e., 87–146 J/mm 3 , on the characteristics of the TiC/TiB 2 laser clads was investigated, and the following conclusions were drawn: The average thickness of the laser-cladded layer is around 0.1 mm, in the range between 0.035 mm and 0.145 mm. The average thickness of the melted alu- minum beneath the laser-cladded layer is around 0.15 mm, in the range between 0.05 mm and 0.220 mm. The increasing of the EEDV influences larger scattering of the cladded-layer thickness, whereas the decreasing of the EEDV influences the decrease of its surface rough- ness. An improvement in the surface mechanical properties was achieved. The average hardness of the 0.1-mm-thick layer was 400±10 HV 0.3. In addition, color chemical etching using Weck’s reagent was performed to study the sensitivity of the etchant to microstructure inhomogeneities of the laser- treated aluminum alloy. Color etching using Weck’s reagent was shown to be a very sensitive qualitative metallographic tool. It highlights many details of the laser-affected areas. The penetration depth, melting pool, their boundaries and various morphological and compositional inhomo- geneities could be clearly distinguished. The sensitivity of the used color etchant to the morphological and com- positional differences was confirmed by FE-SEM/EDS analyses and microhardness measurements. The silicon segregations in laser-affected aluminum are colored with bluish colors. This additional information suggests that the method can be used for metallographic characterization in combination with more expensive and sophisticated analytical methods. Acknowledgments This work was carried out within the framework of the programs P2-0132 and P2-0270 of the Slovenian Research Agency, whose financial support is gratefully acknowledged. Authors gratefully acknowledge Mr. Janez Su{nik, PhD for performing the experimental part of the laser cladding. 5 REFERENCES 1 J. Mazumder, Laser heat treatment: The state of the art, JOM 35 (1983), 18–26 2 L. R. Katipelli, A. Agarwal, N. B. Dahotre, Laser surface engineered TiC coating on 6061 Al alloy: microstructure and wear, Appl. Surf. Sci. 153 (2000), 65–78, doi:10.1016/S0169-4332(99)00368-2 3 M. M. Pariona, V. Teleginski, K. dos Santos, E. L. R. dos Santos, A. A. de Oliveira Camargo de Lima, R. Riva, AFM study of the effects of laser surface remelting on the morphology of Al-Fe aerospace alloys, Mat. Char. 74 (2012), 64–76, doi:10.1016/j.matchar.2012. 08.011 4 L. Thijs, K. Kempen, J. P. Kruth, J. Van Humbeeck, Fine-structured aluminium products with controllable texture by selective laser melting of pre-alloyed AlSi10Mg powder. Acta Mat. 61 (2013), 1809–1819, doi:10.1016/j.actamat.2012.11.052 5 L. M. Laorden, P. Rodrigo, B. Torres, J. Rams, Modification of microstructure and superficial properties of A356 and A356/10%SiCp by Selective Laser Surface Melting (SLSM), Surf. Coat. Tech., 309 (2017), 1001–1009, doi:10.1016/j.surfcoat.2016. 10.046 6 R. [turm, M. [tefanikova, D. Steiner Petrovi~, Influence of pre- heating on the surface modification of powder-metallurgy processed cold-work tool steel during laser surface melting, Appl. Surf. Sci. 325 (2015), 203–210, doi:10.1016/j.apsusc.2014.11.050 7 J. R. Lawrence, D. G. Waugh, (Ed.), Laser surface engineering, 1st ed., Processes and Applications, Woodhead Publishing, Amsterdam 2015, 1–718 8 A. Buling, H. Sändker, J. Stollenwerk, U. Krupp, A. Hamann-Stein- meier, Laser surface pretreatment of 100Cr6 Bearing Steel – Hardening effects and white etching zones, Appl. Surf. Sci. 378 (2016), 564–571, doi:10.1016/j.apsusc.2016.03.088 9 I. Maskery, N. T. Aboulkhair, M. R. Corfield, C. Tuck, A. T. Clare, R. K. Leach, R. D. Wildman, I. A. Ashcroft, R. J. M. Hague, Quanti- fication and characterization of porosity in selectively laser melted Al-Si10-Mg using X-ray computed tomography, Mat. Char. 111 (2016), 193–204, doi:10.1016/j.matchar.2015.12.001 D. STEINER PETROVI^, R. [TURM: SENSITIVITY OF WECK’S REAGENT TO THE MICROSTRUCTURE INHOMOGENEITIES ... 692 Materiali in tehnologije / Materials and technology 52 (2018) 6, 687–693 10 A. H. Wang, C. S. Xie, J. H. Nie, Bond strength of a laser-clad iron- base alloy coating on Al-Si alloy substrate and its fracture behavior, Mat. Char. 47 (2001), 1–7, doi:10.1016/S1044-5803(01)00145-0 11 A. H. Wang, C. S. Xie, W. Y. Wang, Cracking behavior in the transi- tional region of laser-clad coatings on Al-Si alloy under multiple impact loading, Mat. Char. 49 (2003), 247–254, doi:10.1016/ S1044-5803(03)00014-7 12 J. A. Varela, J. M. Amado, M. J. Tobar, M. P. Mateo, A. Yañez, G. Nicolas, Characterization of hard coatings produced by laser cladding using laser-induced breakdown spectroscopy technique, Appl. Surf. Sci. 336 (2015), 396–400, doi:10.1016/j.apsusc.2015. 01.037 13 M. Barekat, R. S. Razavi, A. Ghasemi, Nd:YAG laser cladding of Co-Cr-Mo alloy on -TiAl substrate, Opt. Laser Technol. 80 (2016), 145–152, doi:10.1016/j.optlastec.2016.01.003 14 K. Zhang, J. Zou, J. Li, Z. Yu, H. Wang, Surface modification of TC4 Ti alloy by laser cladding with TiC+Ti powders, Trans. Nonferrous Met. Soc. China 20 (2010), 2192–2197, doi:10.1016/S1003-6326 (09)60441-6 15 R. Anandkumar, A. Almeida, R. Vilar, Wear behavior of Al–12Si/ TiB2 coatings produced by laser cladding, Surf. Coat. Tech., 205 (2011), 3824–3832, doi:10.1016/j.surfcoat.2011.01.048 16 R. Anandkumar, A. Almeida, R. Vilar, Microstructure and sliding wear resistance of an Al–12 wt.% Si/TiC laser clad coating, Wear, 282–283 (2012), 31–39, doi:10.1016/j.wear.2012.01.022 17 D. Ravnikar, N. B. Dahotre, J. Grum, Laser coating of aluminum alloy EN AW 6082-T651 with TiB2 and TiC: Microstructure and mechanical properties, Appl. Surf. Sci. 282 (2013), 914–922, doi:10.1016/j.apsusc.2013.06.089 18 Y. Diao, K. Zhang, Microstructure and corrosion resistance of TC2 Ti alloy by laser cladding with Ti/TiC/TiB2 powders, Appl. Surf. Sci. 352 (2015), 163–168, doi:10.1016/j.apsusc.2015.04.030 19 J. Su{nik, J. Grum, R. [turm, Effect of pulse laser energy density on TiC cladding of aluminium substrate, Teh. Vjes., 22 (2015), 1553–1560, doi:10.17559/TV-20150221215735 20 A. Farnia, F. M. Ghaini, J. Sabbaghzadeh, Effects of pulse duration and overlapping factor on melting ratio in preplaced pulsed Nd:YAG laser cladding, Opt. Lasers Eng. 51 (2013), 69–76, doi:10.1016/ j.optlaseng.2012.07.015 21 C. K. Sahoo, M. Masanta, Effect of pulse laser parameters on TiC reinforced AISI 304 stainless steel composite coating by laser surface engineering process, Opt. Lasers Eng. 67 (2015), 36–48, doi:10.1016/j.optlaseng.2014.10.010 22 S. Vazehrad, J. Elfsberg, A. Dioszegi, Study of microstructure and silicon segregation in cast iron using color etching and electron microprobe analysis, Mat. Char. 104 (2015), 132–138, doi:10.1016/ j.matchar.2014.09.008 23 A. Riquelme, P. Rodrigo, M. D. Escalera-Rodriguez, J. Rams, Analysis and optimization of process parameters in Al-SiCp laser cladding, Opt. Lasers Eng. 78 (2016), 165–173, doi:10.1016/ j.optlaseng.2015.10.014 24 L. Gao, Y. Harada, S. Kumai, Microstructural characterization of aluminium alloys using Weck’s reagent, part I: Applications, Mat. Char. 107 (2015), 426–433, doi:10.1016/j.matchar.2015.01.005 25 L. Gao, Y. Harada, S. Kumai, Microstructural characterization of aluminium alloys using Weck’s reagent, part II: Coloring mechanism, Mat. Char. 107 (2015), 434–452, doi:10.1016/j.matchar. 2015.05.006 26 R. Vilar, E. C. Santos, P. N. Ferreira, N. Franco, R. C. da Silva, Structure of NiCrAlY coatings deposited on single-crystal alloy turbine blade material by laser cladding, Acta Mat., 57 (2009), 5292–5302, doi:10.1016/j.actamat.2009.06.049 D. STEINER PETROVI^, R. [TURM: SENSITIVITY OF WECK’S REAGENT TO THE MICROSTRUCTURE INHOMOGENEITIES ... Materiali in tehnologije / Materials and technology 52 (2018) 6, 687–693 693