In this work mechanical properties and microstructure of duplex steel after heat treatment are shown. Heat treatment of the steel consisted of water quenching from 1050°C. A ferrite-austenite microstructure was obtained and the brittle ?$\sigma$?-phase was avoided. The results show that the impact energy depends on the direction of rolling. In rolling direction the share of ferrite and austenite was approximately equal.

Rights

URN

URN:NBN:SI:doc-1OSRYJTJ

COBISS ID

37034

Added

22.07.2011

Metadata

Citation

APA:

Gojić, Mirko, Kosec, Ladislav, Vehovar, Leopold (1997). Mechanical and microstructural properties of duplex steel, volume 31, issue 6. URN:NBN:SI:doc-1OSRYJTJ from http://www.dlib.si

MLA:

Gojić, Mirko, Kosec, Ladislav, Vehovar, Leopold. Mechanical and microstructural properties of duplex steel. Inštitut za kovinske materiale in tehnologije
Železarna Jesenice
Železarna Ravne
Železarna Štore, 1997.
<http://www.dlib.si/?URN=URN:NBN:SI:doc-1OSRYJTJ>

Kovine zlitine tehnologije
1992-1999
(Assembly record)

prejšnja

Methods for the validation of advanced thin hard protective coatings - an European program
1997
(Previous issue)

naslednja

The difference between the magneto-crystalline anisotropy of the intermetallic alloy Prsub2(Cosub0.5Fesub0.5)sub17 and interstitially modified Prsub2(Cosub0.5Fesub0.5)sub17Nsub(3-delta)
1997
(Next issue)

Mechanical and microstructural properties of duplex steelMikrostruktura in mehanske lastnosti dupleks jekel

Mechanical and microstructural properties of duplex steel
Mikrostruktura in mehanske lastnosti dupleks jekel