Powder, filaments and ribbons of NiAl 12,5 (wt.%) alloy were manufactured by melt spinner at different speed of copper wheel, up to 20,5 m/s. The thickness of the ribbon was between 14 and 60 ?$\mu$?m. Morphology of the as cast structure and the microstructural characteristics were observed and tensile strength of the ribbon was tested.

Rights

URN

URN:NBN:SI:DOC-84SNJLS8

COBISS ID

17101573

Added

22.07.2011

Metadata

Citation

APA:

Torkar, Matjaž, Šuštaršič, Borivoj (1995). Sinteza intermetalne zlitine NiAl 12,5, volume 29, issue 1/2. URN:NBN:SI:DOC-84SNJLS8 from http://www.dlib.si

MLA:

Torkar, Matjaž, Šuštaršič, Borivoj. Sinteza intermetalne zlitine NiAl 12,5. Inštitut za kovinske materiale in tehnologije
Železarna Jesenice
Železarna Ravne
Železarna Štore, 1995.
<http://www.dlib.si/?URN=URN:NBN:SI:DOC-84SNJLS8>

Kovine zlitine tehnologije
1992-1999
(Assembly record)

prejšnja

Nizkoenergijski pospeševalnik pri analizah materialov
1995
(Previous issue)

naslednja

Ultra in ekstremni visoki vakuum
1995
(Next issue)