DOI: 10.17344/acsi.2014.1056 Acta Chim. Slov. 2015, 62, 281-287 281 Scientific paper Preparation of Electrically Conductive Au Thin Films by Colloid Sedimentation V Ur{a Petek, Peter Bukovec and Irena Kozjek [kofic* Faculty of Chemistry and Chemical Technology, University of Ljubljana, Vecna pot 113, SI-Ljubljana, Slovenia * Corresponding author: E-mail: irena.kozjek-skofic@fkkt.uni-lj.si Received: 09-25-2014 Dedicated to the memory of Prof. Dr. Jurij V. Brencic. Abstract A novel and facile wet-chemical method for the preparation of Au thin films is presented. The Au thin films were deposited on glass substrates by the gravitational sedimentation of Au colloids. The colloids were formed by chemical reduction in ethanol using HAuCl4 and NaBH4 with no added surfactants. Without stabilizing agents the colloids quickly aggregated, settled to the bottom and formed a thin film. The sedimentation of the colloids was monitored using UV-vis spectroscopy. Thin films with Au loads ranging between 0.25 and 4.0 g m-2 were prepared and characterized by means of UV-vis spectroscopy, electrical resistance measurements, optical microscopy, scanning electron microscopy, and cyclic voltammetry. The results showed that nanostructured Au films with a very high specific surface area were formed. The films were electrically conductive and partially transparent to visible light. Keywords: Gold, Colloid, Sedimentation, Thin film, Cyclic voltammetry, Electrical resistance 1. Introduction Ever since 1857, when Michael Faraday studied thin Au films on glass and their interaction with visible light, Au thin films have been intensively investigated.1 They can be used as catalysts, sensors, biosensors, and substrates for surface-enhanced Raman spectroscopy (SERS).2-5 Au thin films on glass also have the potential to be used as transparent conductive electrodes (TCEs) in solar cells, and infrared reflective coatings for architectural win-dows.6,7 Different applications require different properties of the Au thin films. For example, they must be continuous in order to act as conductive corrosion-protection coatings for electrical contacts in electronic devices.8 In photovoltaic devices, the films have to be highly conductive and highly transparent. A large specific surface area is crucial for Au films that are to be used as electrochemical sensors or catalysts. In optical sensing, specific optical properties are required, which are characteristic for films with isolated Au nanoparticles. The optical, electrical and catalytic properties of Au films strongly depend on their morphology and on their method of preparation. Many different methods have been developed for the deposition of Au films with the desired morphology. Some common methods for Au deposition on glass include sputtering, evaporation, and chemical vapour deposition.9-11 These methods enable the preparation of Au films with controlled morphologies and thicknesses, ranging from atomic monolayers to continuous Au films that are several hundred nanometres thick. However, for this, specialized equipment and high-vacuum conditions are required. Electrochemical deposition is a widely used technique for Au coating, but it requires an electrically conductive substrate and is therefore not applicable for depositing Au on glass. Screen-printing is a commonly used method for the deposition of cheap, large-scale, Au thin films. However, electrochemical behavior of commercially available, screen-printed Au films, can be strongly influenced by the chemicals used in the inks and treatments of the films, which are usually not disclosed.12 In addition to these methods, wet-chemical procedures have also been extensively studied. They require no specialized equipment or vacuum and can be used to deposit Au films on non-conductive substrates. In electro-less deposition, Au films are formed by the reduction of Au ions on a glass surface rather than by a homogeneous reduction in solution.13 A pre-treatment of the glass is ne- Petek et al.: Preparation of Electrically Conductive Au Thin Films 282 Acta Chim. Slov. 2015, 62, 281-287 cessary in order to form catalytic sites for the reduction of the Au precursor. Another approach is to form Au nano-particles in solution and subsequently immobilize them on the glass surface. Au nanoparticles are most commonly attached to the glass by functionalising its surface with thiol, amino or cyano functional groups, to which the Au nanoparticles strongly adhere and form a monolayer.14 Mul-tilayered nanoparticle films can be obtained using Afunctional linkers to attach additional layers of Au nanopartic-les to the preformed monolayer in a so-called layer-by-layer deposition.15 The adhered nanoparticle monolayers can also serve as nucleation sites for the subsequent reduction of Au ions from solution using a seed-and-growth method, thus increasing their size and causing them to coalesce into continuous Au films.16 In the present work, we focused on a novel method for thin-film preparation based on colloid sedimentation. This method enables the facile preparation of electrically conductive, nanostructured, Au films on glass. To the best of our knowledge, no Au or other metallic thin films have yet been prepared by colloid sedimentation. The only similar deposition technique is the so-called snow-globe (SG) method, which was reported for the deposition of thick titania films by the sedimentation of micrometre-sized particles.17 2. Experimental 2. 1. Materials and Methods HAuCl4 • xH2O was purchased from Fluka Chemica and NaBH4 was purchased from Merck-Schuchardt (> 96%). Both were used without further purification. Absolute ethanol (puriss, > 99.5%) and deionized water were also used. Microscope glass slides (Micro slides, 26 x 76 mm) were employed as the substrates for the thin-film deposition. They were cut to appropriate dimensions (10 mm x 26 mm), cleaned in an ultrasonic bath in absolute ethanol (5 min) and then dried. The UV-vis spectra were recorded using a Varian UV-vis spectrophotometer Cary 50. The absorbance spectra of the colloidal Au in ethanol were measured in a plastic cuvette from 300 to 700 nm (step 2 nm, scan rate 9600 nm min-1). The beam crossed the colloid at 0.5 cm from the surface. The transmittance spectra of the Au thin films on glass were also measured. A spectrum from a cleaned glass substrate was set as 100% transmittance. Five spectra of each sample were recorded, each at a slightly different area of the sample to obtain an average spectrum of the Au thin film. Three different film samples for every Au load were measured. The morphologies of the Au thin films were studied on an Euromex optical microscope ME 2665 and on a scanning electron microscope (SEM) Zeiss ULTRA plus. The electrical resistance of the Au thin films was measured with a Duwi digital multimeter. An Au-coated glass substrate was strongly pressed face-down onto two sheets of conductive Al foil that were attached on a flat nonconductive material (paper) (Fig. 1). They were 1.0 cm apart and separated by the paper. Each electrode of the multimeter was contacted with one of the Al sheets. The electrical resistance of 1.0 cm2 of the middle section of the Au film was thus measured. Five measurements were made for each sample by slightly changing the position of the sample on the Al foils. Three samples of every Au load were measured. This method enabled a good internal comparison of the resistance of a square surface area of the samples. The measurements gave, in principle, sheet resistance of the films. However, the results are simply referred to as resistance since the method was not standard and the contact resistance was neglected. Figure 1. Resistance measurement of 1.0 cm2 of Au thin film on glass substrate. Cyclic voltammetry measurements were conducted at room temperature using a potentiostat PGSTAT 302N and a three-electrode cell. 60 mL of the 0.1 M phosphate buffer electrolyte with pH 7.4 (77 mM Na2HPO4 and 23 mM NaH2PO4) was purged with N2 gas for approximately 10 min prior to the measurements. The samples of Au films on glass substrates were used as the working electrodes. They were rinsed with deionised water before they were placed in the electrolyte. Each sample was fastened with a metal screw into a conductive metal holder. A piece of Al foil was used to maximize the contact (Fig. 2). The sample was then partly sunk into the electrolyte. Approximately 0.5 cm2 of Au-coated surface was exposed to the electrolyte solution. This was achieved by protecting parts Figure 2. A scheme of the Au thin film on glass during the electrochemical measurements. Petek et al.: Preparation of Electrically Conductive Au Thin Films ... 283 Acta Chim. Slov. 2015, 62, 281-287 of the Au film with a thin shellac coating, applied with a gentle brush and dried in air. A flat Pt electrode with a geometric surface of about 5 cm2 was used as the counter electrode and a Ag|AgCl electrode with a saturated KCl solution was used as the reference electrode. The samples were first activated by cycling 50 times in the potential range from -1.0 to 1.3 V, starting from 0 V in the positive direction with a scan rate of 100 mV s-1. After this initial cycling, additional measurements of the samples were performed in the range from -0.2 to 1.2 V with a scan rate of 10 mV s-1, starting from 0 V in the positive direction. 2. 2. Preparation of the Au Colloids An aqueous HAuCl4/HCl solution (50 mM HAuCl4) was prepared by dissolving HAuCl4 • xH2O in 0.05 M HCl. It was stable for several weeks. Separately, an aqueous Na-BH4/NaOH solution (250 mM NaBH4) was prepared by dissolving NaBH4 in 0.1 M NaOH several minutes before being used. Acidic and alkaline conditions were used to slow down the hydrolysis of HAuCl4 and NaBH4, respecti-vely.18,19 Typically, 20 mL of Au colloid was prepared in a 50 mL beaker by adding 200 pL of NaBH4/NaOH solution to 19.60 mL of ethanol under magnetic stirring at 600 rpm. After 30 s, 200 pL of HAuCl4/HCl was added and the stirring was continued for 10 s. A grey, turbid suspension was immediately formed. The concentration of Au in the colloids was the same in all the experiments (0.50 mM). 2. 3. Deposition of the Au Thin Films The Au suspension was immediately transferred to a flat-bottomed vessel that contained a cleaned glass substrate at the bottom (Fig. 3). The suspension was left to settle for several hours on a horizontal surface. A grey or black sediment (depending on the Au load) was formed on the glass substrate. Since any movement of the liquid could distort the formation of the Au film, the vessel was not moved during the sedimentation. When the colloid completely settled, the clear and colourless solution was carefully removed and the Au film was left to dry at room temperature for several hours. Thin films with different Au loads on the glass were prepared, ranging from 0.25 to 4.0 g m-2. The Au load was determined by the height of Figure 3. A scheme of the Au thin-film deposition on a glass substrate based on the sedimentation of colloidal Au in ethanol. the sedimenting colloid, which ranged between 0.25 and 4.0 cm, respectively. After drying the samples were heated in air at 100 °C for 1 h. The thin films had poor adhesive properties and could be completely removed from the glass surface by gentle wiping or with a scotch tape. The samples were nevertheless stable enough to undergo the handling and the characterization. Their adhesion improved somewhat with the thermal treatment and aging. The weak adhesion of Au on glass is well-documented in the literature.20 Au films were also prepared on flexible plastic substrates. They showed similar properties and behaviour as the films on glass, but the results are not reported in this study. 3. Results and Discussion 3. 1. Optical Properties of the Au Colloid The sedimentation of the colloid was monitored by measuring its absorbance minimum at 480 nm as a function of time after the reduction of HAuCl4 (Fig. 4 a). The b) 0.1 - 0.0 1 min 5 min 10 min 25 min 65 min 300 min 300 400 500 Wavelength / nm 600 700 Figure 4. a) Absorbance of Au colloid (0.50 mM Au, 1 mL) at 480 nm as a function of time after the addition of HAuCl4/HCl to the NaBH4/NaOH solution. b) Time-resolved UV-vis absorbance spectra of the same colloid. Petek et al.: Preparation of Electrically Conductive Au Thin Films ... 284 Acta Chim. Slov. 2015, 62, 281-287 absorbance dropped significantly in the first 15 min of sedimentation, which suggests the formation of large Au aggregates. It can also be assumed that the aggregates were polydispersed and therefore sedimented at different rates. This is reflected in a slowly decreasing absorbance, noticeable after 15 min. After 5 h the colloid completely settled, yet there was still a notable absorbance measured. This was attributed to the adsorption of small amounts of Au on the plastic cuvette walls. From the absorbance spectra of the colloid during sedimentation (Fig. 4 b) it can be confirmed that the reduction of HAuCl4 was completed within the first minute after the addition of HAuCl4 to the NaBH4 solution. If the reduction had not been complete, there would have been a detectable peak at ~ 315 nm due to the absorbance of the [AuCl4]- ions.21 The time-resolved absorbance spectra (Fig. 4 b) also showed that the shape of the spectra did not change significantly with time. The spectra of Au nanoparticles in colloids usually show a strong absorption peak at approximately 520 nm, which is caused by the localised surface pla-smon resonance. This absorbance of green light gives Au nanoparticles their typical red colour.22 The absence of a strong plasmon resonance peak in the recorded absorban-ce spectra and the grey colour of the colloids suggested that large Au particles (aggregates) in the micrometre range were formed, rather than individual nanoparticles. This was also confirmed by the rapid sedimentation, detected as a strong absorbance drop that quickly followed the reaction (Fig. 4 a). Since the structure of the sediments normally reflects the structure of the aggregates that are formed in a colloid, the shape and size of the aggregates can be estimated from morphological analyses of the Au thin films. 3. 2. Morphologies of the Au Thin Films The images of the Au thin films taken with the optical microscope (Fig. 5) revealed the morphology of the Au thin films. Films with low Au loads (0.25-1.0 g m-2) consisted of interconnected Au-island structures on the glass. With an increasing Au load, the patches of uncovered glass surface decreased and at high Au loads (> 2.0 g m-2) the substrates were almost entirely covered by a Au layer. The SEM micrographs in Fig. 6 show that the small features of Au were in the nanometre domain. This suggests a very high specific surface area of the Au films. Overall, the observations of the thin-film morphologies revealed that fractal aggregates of irregular size and shape in the size range of 100 pm were formed in the colloid. This confirms that rapid aggregation took place immediately after the reduction of the HAuCl4 precursor. Rapid aggregation typically leads to fractal aggregates of large dimensions.23 This is to be expected, since no stabilizer was added to the system. ¿fí ' V'^HB'' > 0.50 TPS Íf^Pf f* J\ * ■ •> 2.5 V * 3 5 imm Figure 5. Optical microscope images of Au (dark) thin films on glass (light) with different Au loads (given in g m-2). Figure 6. SEM micrographs of Au thin films with 1.0 g m 2 Au (light) on glass (dark) showing features with nano dimensions. 3. 3. Optical Properties of the Au Thin Films The films appeared grey or black (depending on the Au load) in transmitted light. However, in reflected light they appeared dark brown. This observation can be explained by consulting the transmittance spectra of the films (Fig. 7 a). Transmittance was lower at shorter wavelengths, which means that violet and blue light were more strongly attenuated than the other colours and complementary yellow and orange shades could be observed, which are a typical colour for bulk Au. The transmittance of the samples (measured at its maximum at 490 nm) naturally decreases with an increasing Au load (Fig. 7 b). The strongest decrease in tran- Petek et al.: Preparation of Electrically Conductive Au Thin Films ... 285 Acta Chim. Slov. 2015, 62, 281-287 Au load / g m Figure 7. a) UV-vis transmittance spectra of Au thin films on glass with various Au loads. b) Transmittance of Au thin films on glass at 490 nm. smittance is visible in the Au-load range from 0.25 to 1.5 g m-2, which can be attributed to strong morphological changes, from individual Au islands to an almost continuous, porous, Au film with small patches of uncovered glass. The highest transmittance obtained was slightly above 60% (Au load 0.25 g m-2). Compared to the tran-smittance of the Au coatings, which are considered for transparent conductive electrodes (such as nanotrough or nanowire assemblies) this is very low. A transmittance higher than 90% is required for commercial applications.24,25 3. 4. Electrical Resistance of the Au Thin Films The electrical resistance of the thin films strongly depended on their morphology. Even films with small Au loads were conductive due to the continuous metallic pathways between the Au islands (Fig. 5). With an increasing Au load these connections became more numerous and the electrical resistance therefore significantly decreased (Fig. 8). Figure 8. Resistance of Au thin films on glass with various Au loads before (black) and after (red) a thermal treatment at 100 °C for 1 h. A resistance drop over several orders of magnitude was observed when the Au loads were increased from 0.25 g m-2 to 1.5 g m-2 (from kQ to 10 Q, respectively). With a further increase in the Au loads the resistance decreased only slightly, which was attributed to the increasing film thickness. This was confirmed by calculating the resistivity of the films, taking into account the theoretical average thickness of the Au films and the dimensions of the measured film area (1.0 cm x 1.0 cm). The resistivity of films with loads larger than 2.0 g m-2 was approximately 1 |jQ m. This value was much higher than the resistivity of bulk Au (2.4410-8 Q m).26 The higher resistivity can be partially attributed to systematic errors in the resistance measurements (e.g. the contact resistance between the multimeter electrodes, the Al foil with its surface oxide layer and the Au film) as well as the nanoporous structure of the films. It is well known that nanostructured metals have a higher resistivity than the bulk material due to the scattering of electrons on the surface and the particle boundaries.27 A thermal treatment at 100 °C for 1 h did not cause significant changes to the conductivity of the samples with a Au load higher than 1.0 g m-2. It did, however, notably increase the resistance of the samples with a lower Au load. This was unexpected, since heating usually improves the contact between the particles due to atomic diffusion at the interparticle interfaces.28 This observation requires further study. 3. 5. Electrochemical Properties of the Au Thin Films The electrochemical properties of the Au thin films were studied using cyclic voltammetry. All the measured samples were heated at 100 °C for 1 h. This thermal treatment was assumed to improve the adhesion of the Au to the glass. All the samples were first conditioned by 50 po- Petek et al.: Preparation of Electrically Conductive Au Thin Films ... 286 Acta Chim. Slov. 2015, 62, 281-287 tential cycles in range from -1.0 to 1.3 V, with a scan rate of 100 mV s-1. Cyclovoltammograms (CVs) showed a broad anodic peak (Fig. 9 a) starting at 0.8 V and a corresponding cathodic peak between 0.7 and 0.1 V. The anodic peak was attributed to the formation of a monolayer of gold oxide, which was in turn reduced in the reverse cy- Figure 9. a) CVs of the first 50 cycles of the Au thin film (1.0 g m-2) during initial cycling. b) CVs of Au thin films after initial cycling with varying Au loads. c) Surface roughness of Au thin films calculated from the integrated cathodic peaks. cle.29 With an increasing number of cycles the current peak density strongly increased, which can be attributed to the higher surface roughness, caused by the oxidation and reduction cycles. After 50 cycles the peak current was stabilized. The shape as well as height of the anodic peak changed during the cycling. The position of the cathodic peak shifted slightly towards more negative potentials, which could be due to the morphological changes of the films or simply because of the ohmic drop, which increased with the increasing current density. After initial cycling, new CVs of the films were recorded (in the potential range from -0.2 to 1.2 V, scan rate 10 mV s-1) (Fig. 9 b) in order to determine the surface roughness of the samples, which is the ratio between the real surface area and the geometric surface area (0.5 cm2). The surface-roughness determination was based on the assumption that a gold oxide monolayer was formed during the anodic potential scan and that it was stripped during the reduction in the cathodic scan. By integrating the cathodic peak area and thus determining the exchanged charge, an estimation of the real surface area can be made. A value of 450 ^C cm-2 was reported in the literature and was used in the calculations. Since the oxide coverage can be affected by the measuring conditions (such as the buffer solution, scan rate, potential range, exposed crystal planes, etc.) and significantly different numbers are reported in the literature, this method is not reliable in the absolute sense.30-33 However, if measured under the same conditions, a relative comparison between the samples can be made. Higher peak-current densities are observed for samples with a higher Au load. Estimations of surface roughness, based on the area under the reduction peaks, reveal that the surface roughness increased in proportion to the Au load (Fig. 9 c). This shows that even films with a high Au load retained their porous structure as opposed to coalescing into denser films. The specific surface area was calculated for all the measured samples and was found to be 15 ± 2 m2 g-1, irrespective of the Au load. Some samples showed morphological changes after cycling, some of them even became partially removed. 4. Conclusions A proof-of-principle research was conducted to show that colloid sedimentation can be an efficient method for the preparation of metallic thin films. Nanostruc-tured Au thin films with high specific surface area were made on glass by the gravitational settling of Au colloids in ethanol. The films were weakly adhered to the glass surface. By varying the amount of settling colloids, films with different Au loads were formed, which ranged from transparent networks of individual Au islands with a relatively high transmittance (> 60%) and electrical resistance a) >- o.o -1.0- -1" cycle - 5lh cycle -10'" cycle -20,h cycle 50th cycle -0.5 0.0 0.5 Potential / V (vs. Ag|AgCI electrode) b) < E 1.0 0.5 0.0 -0.5 -1.0 -0.25 g m -1.0g m "2 -2.0 g m"2 3.0 g m"2 -4.0 g m"2 -0.2 0.0 0.2 0.4 0.6 0.8 1.0 Potential / V (vs. Ag|AgCI electrode) C) 80 t 3 OT Au load / g m' Petek et al.: Preparation of Electrically Conductive Au Thin Films ... 287 Acta Chim. Slov. 2015, 62, 281-287 (> kQ) to highly porous, black continuous layers with a low electrical resistance (4 Q). 5. Acknowledgments This work was supported by the Slovenian Research Agency (research programme P1-0134-0103). 6. References 1. M. Faraday, Trans. R. Soc. 1857, 147, 145-181. 2. A. F. Lamic-Humblot, P. Barthe, G. Guzman, L. Delannoy, C. Louis, Thin Solid Films 2013, 527, 96-101. http://dx.doi.org/10.10167j.tsf.2012.11.096 3. M. M. Collinson, ISRNAnal. Chem. 2013, 2013, 692484. 4. Y. Li, H. J. Schluesener, S. Xu, Gold Bull. 2010, 43, 29-41. http://dx.doi.org/10.1007/BF03214964 5. A. Bouvrée, A. D. Orlando, T. Makiabadi, S. Martin, G. Lo-uarn, J. Y. Mevellec, B. Humbert, Gold Bull. 2013, 46, 283-290. http://dx.doi.org/10.1007/s13404-013-0127-4 6. A. Morag, L. Philosof-Mazor, R. Volinsky, E. Mentovich, S. Richter, R. Jelinek, Adv. Mater. 2011, 23, 4327-4331. http://dx.doi.org/10.1002/adma.201101290 7. X. Xu, T. H. Gibbons, M. B. Cortie, Gold Bull. 2006, 39, 156-165. http://dx.doi.org/10.1007/BF03215549 8. J. Song, L. Wang, A. Zibart, C. Koch, Metals 2012, 2, 450-477. http://dx.doi.org/10.3390/met2040450 9. J. Siegel, O. Lyutakov, V. Rybka, Z. Kolská, V. Svorcík, Na-noscale Res. Lett. 2011, 6, 96. http://dx.doi.org/10.1186/1556-276X-6-96 10. T. Roland, A. Khalil, A. Tanenbaum, L. Berguiga, P. De-lichere, L. Bonneviot, J. Elezgaray, A. Arneodo, F. Argou, Surf. Sci. 2009, 603, 3307-3320. http://dx.doi.org/10.1016Zj.susc.2009.09.021 11. R. G. Parkhomenko, N. B. Morozova, G. I. Zharkova, Y. V. Shubin, S. V. Trubin, V. V. Kriventsov, B. M. Kuchumov, T. P. Koretskaya, I. K. Igumenov, Chem. Vap. Deposition 2012, 18, 336-342. http://dx.doi.org/10.1002/cvde.201207004 12. R. García-Gonzáleza, M. T. Fernández-Abedula, A. Perníab, A. Costa-García, Electrochim. Acta 2008, 53, 3242-3249. http://dx.doi.org/10.1016/j.electacta.2007.07.059 13. J. Hu, W. Li, J. Chen, X. Zhang, X. Zhao, Surf. Coat. Tech-nol. 2008, 202, 2922-2926. http://dx.doi.org/10.1016/j.surfcoat.2007.10.026 14. K. C. Grabar, R. G. Freeman, M. B. Hommer, M. J. Natan, Anal. Chem. 1995, 67, 735-743. http://dx.doi.org/10.1021/ac00100a008 15. P. Kumlangdudsana, A. Tuantranont, S. T. Dubas, L. Dubas, Superlattices Microstruct. 2012, 52, 1043-1051. http://dx.doi.Org/10.1016/j.spmi.2012.07.006 16. Y. Jin, X. Kang, Y. Song, B. Zhang, G. Cheng, S. Dong, Anal. Chem. 2001, 75, 2843-2849. http://dx.doi.org/10.1021/ac001207d 17. A. Basch, F. Beck, T. Söderström, S. Varlamov, K. R. Catchpole, Prog. Photovolt: Res. Appl. 2012, 224. 18. S. Wang, K. Qian, X. Z. Bi, W. J. Huang, Phys. Chem. C 2009, 113, 6505-6510. 19. R.E. Davis, E. Bromels, C.L. Kibby, J. Am. Chem. Soc. 1962, 84, 885-892. http://dx.doi.org/10.1021/ja00865a001 20. M. Ghorbanpour, C. Falamaki, J. Nano. Chem. 2013, 3, 66. 21. A. Alshammari, A. Köckritz, V. Narayana Kalevaru, A. Bagabas, A. Martin, Open J. Phys. Chem. 2012, 2, 252-261. http://dx.doi.org/10.4236/ojpc.2012.24033 22. A. Moores, F. Goettmann, New J. Chem. 2006, 30, 1121- 1132. http://dx.doi.org/10.1039/b604038c 23. D. A. Weitz, J. S. Huang, M. Y. Lin, Sung, J. Phys. Rev. Lett. 1985, 54, 1416-1419. http://dx.doi.org/10.1103/PhysRevLett.54.1416 24. H. Wu, D. Kong, Z. Ruan, P.-C. Hsu, S. Wang, Z. Yu, T. J. Carney, L. Hu, S. Fan, Y. Cui, Nat. Nanotechnol. 2013, 8, 421-425. http://dx.doi.org/10.1038/nnano.2013.84 25. P. E. Lyons, S. De, J. Elias, M. Schamel, L. Philippe, A. T. Bellew, J. J. Boland, J. N. Coleman, J. Phys. Chem. Lett. 2011, 2, 3058-3062. http://dx.doi.org/10.1021/jz201401e 26. P. Wißmann, H.-U. Finzel, Springer Tracts Mod. Phys. 2007, 223, 35-52. http://dx.doi.org/10.1007/3-540-48490-6_4 27. Q. G. Zhang, X. Zhang, B. Y. Cao, Appl. Phys. Lett. 2006, 89, 114102. http://dx.doi.org/10.1063/L2338885 28. J. R. Greer, R. A. Street, Acta Mater. 2007, 55, 6345-6349. http://dx.doi.org/10.1016Zj.actamat.2007.07.040 29. K. Juodkazis, J. Juodkazyt, B. Sebeka, A. Lukinskas, Elec-trochem. Commun. 1999, 1, 315-318. http://dx.doi.org/10.1016/S1388-2481(99)00062-4 30. Y. Horng Tan, J. A. Davis, K. Fujikawa, N. Vijaya Ganesh, A. V. Demchenko, K. J. Stine, J. Mater. Chem. 2012, 22, 67336745. http://dx.doi.org/10.1039/c2jm16633j 31. K. Juodkazis, J. Juodkazyt, V. Jasulaitien, A. Lukinskas, B. Sebeka, Electrochem. Commun. 2000, 2, 503-507. http://dx.doi.org/10.1016/S1388-2481(00)00069-2 32. J. C. Hoogvliet, M. Dijksma, B. Kamp, W. P. van Bennekom, Anal Chem. 2000, 72, 2016-2021. http://dx.doi.org/10.1021/ac991215y 33. J. Zhang, M. Oyama, Anal. Chim. Acta 2005, 540, 299-306. http://dx.doi.org/10.1016/j.aca.2005.03.054 Povzetek Za nanos tankih plasti zlata na ravne steklene podlage smo razvili novo in enostavno metodo posedanja koloida. Koloi-de smo pripravili s kemijsko redukcijo HAuCl4 z NaBH4, kot topilo smo uporabili etanol. Ker nismo dodali stabilizatorja, so koloidi hitro agregirali in se posedli na dno posode ter tako ustvarili nanostrukturirane tanke plasti Au. Količino nanesenega zlata smo spreminjali med 0,25 in 4,0 g m-2. Rezultati so pokazali, da z lahko z metodo posedanja koloida pripravimo električno prevodne nanostrukturirane tanke plasti z visoko hrapavostjo, ki delno prepuščajo vidno svetlobo. Petek et al.: Preparation of Electrically Conductive Au Thin Films ...