R. SOKOLÁØ et al.: INFLUENCE OF CLASS C FLY ASH ON THE PROPERTIES OF PLASTIC CLAY ... 107–111 INFLUENCE OF CLASS C FLY ASH ON THE PROPERTIES OF PLASTIC CLAY AND A FIRED BRICK BODY VPLIV DIMNI[KEGA PEPELA RAZREDA C NA LASTNOSTI PLASTI^NE GLINE IN @GANIH OPEK Radomír Sokoláø * , Martin Nguyen Brno University of Technology, Faculty of Civil Engineering, Institute of Technology of Building Materials and Components, Veveøí 331/95, 602 00 Brno, Czech Republic Prejem rokopisa – received: 2019-07-12; sprejem za objavo – accepted for publication: 2019-11-04 doi:10.17222/mit.2019.148 Class C fly ash (CCFA) was used, according to ASTM C618-12a, as an admixture (10 %/w) in calcareous brick clay to determine the difference (in comparison with pure clay) in the clay body plasticity (CCFA increases the water content, decreases the drying shrinkage, drying sensitivity and bulk density of a green body) and in the properties of a fired body (since CCFA acts as a pore-forming agent, we can expect a lower bulk density and better thermal insulation). Due to low firing temperatures of the brick body (850 °C and 1000 °C), there is no risk of an anhydrite decomposition as Class C fly ash does not increase the SO 2 content in flue gas during the firing and efflorescence. Keywords: fly ash, brick body, sulphur-dioxide emissions, firing Avtorji so uporabili dimni{ki pepel razreda C (CCFA), v skladu s standardom ASTM C618-12a, kot dodatek (10 % mas.) v karbonatno glino za opeke, da bi dolo~ili razlike, ki nastopajo v primerjavi z uporabo naravne (~iste) gline. Avtorji so pri~akovali, da bo dodatek vplival tako na plasti~nost surovcev (CCFA namre~ pove~a vsebnost vode, zmanj{a skr~ek po su{enju, ob~utljivost in volumsko gostoto surovcev), kakor tudi na kon~no `gane opeke (sredstvo za tvorbo por namre~ zni`uje volumensko gostoto in pove~a toplotno izolativnost). Zaradi nizkih temperatur `ganja opeke (850 °C in 1000 °C) ni bilo nevarnosti za razpad anhidrita, saj dodatek dimni{kega pepela razreda C ne pove~uje vsebnosti SO 2 v dimnih plinih med `ganjem in kristalizacijo. Klju~ne besede: dimni{ki pepel, opeka, emisije `veplovega dioksida, `ganje 1 INTRODUCTION Class C fly ash (CCFA, fluidized fly ash) is a by-product obtained during the combustion of a coal-limestone finely milled mixture in a fluidized-bed boiler in thermal-power or heating plants at lower temperatures (about 800 °C). The term "fluidized fly ash" is not used in scientific literature – the type of fly ash is usually not specified. Fluidized fly ash is generally called Class C fly ash according to the American Standard ASTM C618-12a (Standard Specification of Coal Fly Ash and Raw Calcined Natural Pozzolan for Use in Concrete), which determines CCFA (Table 1). Table 1: Classification of fly ashes according to ASTM C618-12a Class ,(SiO 2+Al 2O 3+Fe 2O 3)S O 3 LOI C min 50 % max 5 % max 6 % In the Czech Republic, the total production of CCFA is about 1.4 million tons per year. Fluidized technology is one of the most popular methods for burning coal and other sorts of fuel in thermal-power plants in order to limit sulphur-dioxide emissions. Fly ash/clay mixtures for the single-firing technology for dry-pressed ceramic tiles were developed experi- mentally, using kaolinic stoneware clay as the basic raw material and classical high-temperature fly ash. 1,2 The bodies prepared with this method show a high shrinkage after firing, often even in the reduction cores, in com- parison with the standard bodies based on natural-raw materials. We can use CCFA for glass-ceramic materials development. 3,4 Here, CCFA shows a poorer sinterability (higher water absorption, porosity) than in ceramic bodies. 5 Milling of fly-ash mixtures improves the sinter- ing activity. 1,6 The recycling of three different fly ashes (CCFAs with different CaO contents of 6.76–37.80 %) obtained from the coal thermal-power plants was studied for the glass materials. 7 Fly ash from the coal power plant (CCFA with 14.3 % of CaO and 3.6 % of SO 3 – quartz, calcite, hema- tite) was used for the production of bricks in the local brick factory (0–25 % of clay) as fly ash decreases the compressive strength of bricks due to a high porosity (firing at 800 °C); as a result, a low efflorescence was observed in the bricks incorporating fly ash. 8 Environ- mentally friendly bricks containing clay, fly ash (FA) and bottom ash (BA) were developed. An increase in the FA content leads to an increase in the apparent porosity and water absorption; however, it decreases the bulk density Materiali in tehnologije / Materials and technology 54 (2020) 1, 107–111 107 UDK 620.1:662.613.1:666.9.01:691.421.24 ISSN 1580-2949 Original scientific article/Izvirni znanstveni ~lanek MTAEC9, 54(1)107(2020) *Corresponding author's e-mail: sokolar.r@fce.vutbr.cz (Radomír Sokoláø) and thermal conductivity of bricks. The BA content does not have any significant influence on the properties of bricks. All heavy metals were immobilized in the structures of fired bricks. 9 Brick clay, sewage sludge and fly ash (CFFA – 2.33 CaO, 0.3 SO 3 ) were successfully used for the production of brick fired at two different tempera- tures (900 °C and 1050 °C). 10 Municipal solid waste incineration (MSWI) fly ash (36,7 % of CaO as free CaO, Ca(OH) 2 , calcite, quartz) was re-utilized for eco-friendly dry-pressed ceramic-brick production (fired at 1000 °C). 11 The fly ashes (CFFA – 2.26 % of CaO and 0 , 0 3%o fS O 3 ) from the co-combustion of coal and pet coke were used as raw materials to replace clay to make dry-pressed fired (800, 900, 1000) °C bricks. These bricks do not present environmental problems according to a leaching study. 12 Dry-pressed (at 26 MPa) bricks based on pure-lignite fly ash with different granulo- metries were developed and reported in 13 – their produc- tion included a compressive strength of 27–57 MPa and water absorption of 19–25 % depending on the firing temperature in a range of 900–1050 °C. The aim of the article is to define: • The CFFA influence on the properties of a plastic and green body (interaction of brick clay and CFFA) – drying sensitivity, drying shrinkage, working water. • The effect of CFFA in a raw-material mixture used for clay masonry bricks on sulphur oxide SO 2 emissions included in flue gas during the firing (up to 1000 °C and with the soaking time at 1000 °C). • The CFFA influence on the properties of a fired body (at 850–1000 °C, the maximum firing temperatures for bricks) – water absorption, bulk density, firing shrinkage, flexural strength and efflorescence. 2 MATERIALS, SAMPLES AND METHODS Fluidized fly ash CCFA from the thermal-power plant (Tisova-CEZ Group, Czech Republic) and typical brick clay for the THERM clay-masonry-unit (EN 771-1) pro- duction (Novosedly-Wienerberger Group, Czech Repub- lic) were used for the preparation of laboratory samples. The chemical compositions of both used materials (Table 2) are typical and correspond to their mineralo- gical compositions (Figures 3 and 4). CFFA is charac- terized by a high SO 3 content (in the form of anhydrite CaSO 4 ), quartz, calcium oxide CaO and calcite CaCO 3 (Table 3). Brick clay can be characterized by its calcareous nature (the content of calcite is about 12 w/%. according to the thermal analysis – TG, DTG, Mettler Toledo TGA/DSC1 device – the decomposition of calcite in a temperature range of 720–850 °C (Figure 1), and the presence of several clay minerals (kaolinite, illite and montmorillonite), quartz and orthoclase (Figure 3). The mineralogical composition was identified using an X-ray diffraction analysis (XRD; PANALYTICAL Empyrean) with Cu-K as the radiation source, an accelerating voltage of 45 kV , beam current of 40 mA, diffraction angle 2 in a range of 5–80° and step scan of 0.01°. Granulometry of the used materials was determined using the residue on a screen with a size of 63 μm (R 63 ) (Table 3). According to granulometry (Figure 2), brick clay, suitable for the production of thermal insulating masonry THERM units (EN 771-1) was used as the basic plastic material for the preparation of test samples from the plastic body. It contains about 28 % of grains below 2 μm (a sedimentation analysis). R. SOKOLÁØ et al.: INFLUENCE OF CLASS C FLY ASH ON THE PROPERTIES OF PLASTIC CLAY ... 108 Materiali in tehnologije / Materials and technology 54 (2020) 1, 107–111 Table 2: Chemical compositions (in mass fractions, w/ %) of used raw materials – fly ash CCFA (Tisova) and brick clay (Novosedly) Material SiO 2 Al 2 O 3 Fe 2 O 3 TiO 2 CaO MgO MnO K 2 ON a 2 OS O 3 LOI clay 56.4 12.7 4.4 0.1 9.8 3.3 0.1 3.0 1.7 0.6 12.2 CCFA 35.0 23.3 5.5 5.4 21.5 1.6 0.1 0.5 0.1 2.5 4.5 Figure 2: Grain-size classification of used brick clay (black point) according to Winkler's diagram: 14 common bricks, b) vertically per- forated bricks, c) roofing tiles and masonry bricks, d) hollow products Figure 1: TG (solid line) and DTG (dashed line) of brick clay (heating at 10 °C/min). The initial mass of the sample for TG was 69.4548 mg Table 3: Residue of used fly-ash and brick-clay grains on a 63-μm sieve Material R 63 (w/%) clay 16.0 CCFA 25.9 For the preparation of test samples, the average sample of dried brick clay (60 °C) was ground in a laboratory pan mill to get a homogenous fineness of 0–1 mm. Two batches of brick clay and CCFA (0 %/w – N and 10 %/w – N10) were prepared for the experiments. The raw-material mixture (dry-milled clay and CCFA) was dry-mixed for 24 h in the homogenizer. The brick clay (N) and mixture brick clay/CCFA (N10) were moistened to achieve the plasticity that corresponds to the deformation ratio of 0.7 according to K. Pfefferkorn 15 (H f /H 0 where H 0 is the initial height and H f is the final height after the deformation on the Pfefferkorn apparatus). After 24-hour ageing of the plastic clay body, the samples were made by hand, the clay being churned into a metal form with dimensions of (100 × 50 × 20) mm. The drying was conducted in the natural way in the laboratory at a temperature of about 21 °C; the samples were subsequently finally dried in the laboratory drier at a temperature of 110 °C. The established Bigot curve (Figure 5) was used to calculate the drying sensitivity index DSI-B 16 : DSI B ww DS i −= − ⋅ c 100 [-] (1) where: W i is the initial water content of the plastic body during the preparation of test samples [%]; W c is the critical water content of the test samples subtracted from the Bigot curve (Figure 5) (%); DS is the drying shrinkage (%). The samples were fired in the laboratory electric kiln at 850 °C and 1000 °C (3 °C.min –1 with 1-hour soaking time at the maximal temperature), which corresponds to the typical firing temperature interval for clay masonry bricks. The sulphur dioxide (SO 2 ) content in the flue gases was assessed continually during the firing process using a TESTO 340 flue-gas analyser. After the firing, the body properties (water absorption WA, bulk density B and flexural strength R) were defined in accordance with the official testing standard EN ISO 10545. Firing shrinkage FS was calculated with the following Equation (2): FS ll l = −⋅ () fd d 100 [%] (2) where: l d is the length of dried test samples (mm) and l f is the length of fired test samples (mm). The susceptibility to efflorescence was determined in accordance with ASTM C 67 – the test samples were immersed to a constant depth of 10 mm under water at one end. After 7 d, the water was allowed to dry (at 110 °C) in 24 h and observations relating to efflores- cence were recorded. 3 RESULTS AND DISCUSSION According to K. Pfefferkorn, 15 CCFA as an additive to a raw-material mixture increases the water content w r (Table 4), achieving the plasticity of a clay body with a ratio of 0.7 by 4.3 % and, at the same time, reduces the R. SOKOLÁØ et al.: INFLUENCE OF CLASS C FLY ASH ON THE PROPERTIES OF PLASTIC CLAY ... Materiali in tehnologije / Materials and technology 54 (2020) 1, 107–111 109 Figure 4: XRD diffraction of used CCFA Figure 3: XRD diffraction of used brick clay Figure 5: Relationship between drying shrinkage and water content (the Bigot curve) – DSI-B determination drying shrinkage DS, resulting in a reduction in the bulk density BG of a dried green body (Table 4). The drying process of both compared plastic clay bodies (mixtures N and N10) is documented with the Bigot curve – according to Bigot DSI-B, CCFA causes a complete decrease of the clay-body shrinkage when reaching the critical water content and a slight decrease in the sensitivity to drying (Figure 5). Table 4: Properties of the plastic body (w r – water content, DS – drying shrinkage, BG – bulk density of a dried green body) Mixture w r (%) DS (%) BG (kg·m –3 ) N 22.7 –5.3 1430 N10 27.0 –4.7 1400 According to Equation (3): 2CaSO 4 - 2CaO + 2SO 2 +O 2 (3) decomposition of anhydrite CaSO 4 can be expected during the firing of a dry-pressed body based on pure CCFA when the temperature exceeds 1200 °C or about 1000 °C for dry-pressed clay/CCFA mixtures. 17 For this reason, there is a risk of sulphur dioxide leakage during the firing of the N10 samples at higher temperatures, but this was not confirmed (Figure 6). Conversely, the admixture of CCFA resulted in a slight reduction of the SO 2 content of the flue gas. This can be caused by the calcite content in CCFA, which was able to bind sulphur dioxide from the brick clay. The admixture of CCFA in brick clay slightly increases the shrinkage of the test samples during the firing (Figure 7) due to the sintering of body N10 in a range of 800–900 °C compared with body N. We can observe a higher volume increase for the fired body, when CCFA is used (mixture N10), in a temperature range of about 1000–1100 °C – this is typical of an anorthite creation during the firing. 18 CCFA is a source of a higher quantity of anorthite in the fired brick bodies due to the CaO content (Table 2). The main effect of the CCFA addition to brick raw-material mixtures is in the pore-forming ability – there is an evident bulk-density (B) reduction and an increased water absorption (WA) of the body (Table 5) due to the decomposition of calcium carbonate and formation of anorthite, leading to a volume increase (Figure 7). Significantly better thermal-insulation pro- perties of a fired brick body can be expected at both tested firing temperatures (850 °C and 1000 °C) in the case of a CCFA addition to the raw-material mixture (N10) – see the coefficient of thermal conductivity, in Table 5. The efflorescence on the surface of brick specimens after a 7-day immersion in distilled water was docu- mented. No marginal difference (N vs. N10) in the efflorescence was observed on the surface of the samples after drying at 110 °C (Figure 8). Table 5: Properties of fired bodies (R – flexural strength, B–bulk density, WA – water absorption, FS – firing shrinkage) – the effect of the firing temperature Sample Firing (°C) R (MPa) B (kg.m -3 ) WA (%) FS (%) (W/mK) N 850 15.9 1720 23.0 + 1.5 0.5184 1000 12.0 1700 28.3 – 0.1 0.6654 N10 850 12.5 1590 22.9 + 0.3 0.4565 1000 9.8 1560 28.0 – 0.6 0.4666 5 CONCLUSIONS In the Czech Republic, about 1.4 million tons of Class C fly ash (CCFA) are produced per year that are not applied in the production of building materials. The aim of the paper was to verify the applicability of CCFA R. SOKOLÁØ et al.: INFLUENCE OF CLASS C FLY ASH ON THE PROPERTIES OF PLASTIC CLAY ... 110 Materiali in tehnologije / Materials and technology 54 (2020) 1, 107–111 Figure 7: Dilatometric analysis during the firing (3 °C/min without the soaking time) Figure 6: Content of sulphur dioxide (SO 2 ) in flue gas during the firing of test samples Figure 8: Fired samples after the efflorescence test in the brickmaking industry. A mixture of typical calcareous (about 12 %/w/ of calcite) brick clay for the production of clay masonry bricks (Novosedly, Wiener- berger Group, Czech Republic) and 10 %/w of CCFA (Tisova, CEZ Group, Czech Republic) was analysed and compared with a pure-clay brick. CCFA influences the properties of clay-body plasticity (increases the water content, decreases the drying shrinkage, drying sen- sitivity and bulk density of a green body) and a fired body (CCFA acts as a pore-forming agent – we can expect a lower bulk density and better thermal-insulation properties of fired bodies). Due to low firing tem- peratures in the brickmaking industry (in a range of 850–1000 °C) there is no risk of an anhydrite decom- position – Class C fly ash does not increase the SO 2 content in flue gas during the firing and efflorescence. As a source of CaO, CCFA contributes to a higher anorthite content in a fired body. Acknowledgment This article was supported by the Czech Science Foundation GA^R, project No. 18-02815S with project name: Elimination of sulphur oxide emission during the firing of ceramic bodies based on fly ashes of Class C. 6 REFERENCES 1 R. Sokolar, L. Smetanova, Dry pressed ceramic tiles based on fly ash–clay body: Influence of fly ash granulometry and pentasodium triphosphate addition, Ceramic International, 36 (2010) 1, 215–221 2 I. Queralt, X. Querol, A. López-Soler, F. Plana, Use of coal fly ash for ceramics: a case study for a large Spanish power station, Fuel, 76 (1997) 87, 87–791 3 M. Erol, A. Genç, M. L. Öveçolu, E. Yücelen, S. Küçükbayrak, Y . Taptik, Characterization of a glass-ceramic produced from thermal power plant fly ashes, Journal of the European Ceramic Society, 20 (2000) 12, 2209–2214 4 L. Barbieri, I. Lancellotti, T. Manfredini, I. Queralt, J. Ma. Rincon, M. Romero, Design, obtainment and properties of glasses and glass–ceramics from coal fly ash, Fuel, 78 (1999) 2, 271–276 5 M. Erol, S. Küçükbayrak, A. Ersoy-Meriçboyu, Characterization of sintered coal fly ashes, Fuel, 87 (2008) 7, 1334–1340 6 M. Ilic, C. Cheeseman, C. Sollars, J. Knight, Mineralogy and micro- structure of sintered lignite coal fly ash, Fuel, 82 (2003) 3, 331–336 7 M. Erol, S. Küçükbayrak, A. Ersoy-Meriçboyu, Characterization of coal fly ash for possible utilization in glass production, Fuel, 86 (2007) 5–6, 706–714 8 S. Abbas, M. A. Saleem, S. M. S.K. Kazmi, M. J. Munir, Production of sustainable clay bricks using waste fly ash: Mechanical and durability properties, Journal of Building Engineering, 14 (2017) 11, 7–14 9 M. Sutcu, E. Erdogmus, O. Gencel, A. Gholampour, E. Atan, T. Ozbakkaloglu, Recycling of bottom ash and fly ash wastes in eco-friendly clay brick production, Journal of Cleaner Production, 233 (2019), 753–764 10 E. Esmeray, M. Atis, Utilization of sewage sludge, oven slag and fly ash in clay brick production, Construction and Building Materials, 194 (2019) 1, 110–121 11 Y . Deng, B. Gong, Y . Chao, T. Dong, W. Yang, M. Hong, X. Shi, G. Wang, Y . Jin, Z.-G. Chenc, Sustainable utilization of municipal solid waste incineration fly ash for ceramic bricks with eco-friendly biosafety, Materials Today Sustainability, 1–2 (2018) 11, 32–38 12 C. Leiva, C. Arenas, B. Alonso-Fariñas, L. F. Vilchesa, B. Peceño, M. Rodriguez-Galán, F. Baena, Characteristics of fired bricks with co-combustion fly ashes, Journal of Building Engineering, 5 (2016) 3, 114–118 13 K. Pimraska, M. Wilhelm, W. Wruss, A new approach to the production of bricks made of 100 % fly ash, Tile and Brick Int., 16 (2000) 6, 428–433 14 H. G. F. Winkler, Bedeutung der Korngrössenverteilung und des Mineralbestandes von Tonen feur die Herstellung grobkeramischer Erzeugnisse, Berichte der Deutschen Keramischen Gesellschaft, 31 (1954) 10, 337–343 15 K. Pfefferkorn, Ein Beitrag zur Bestimmung der Plastizität in Tonen und Kaolinen, Sprechsaal, 57 (1924) 25, 297–299 16 P. Aungatichart, S. Wada, Correlation between Bigot and Ratzen- berger drying sensitivity indices of red clay from Ratchaburi province (Thailand), Applied Clay Science, 42 (2009) 2, 182–185 17 R. Sokolar, M. Nguyen, The fly ash of class C for ceramic tech- nology, 24 th Conference Construmat 2018, Herlany, Slovakia, IOP Conference Series: Materials Science and Engineering, 385 (2018)1 18 R. Sokolar, L. V odova, S. Grygarova, I. Stubna, P. Sin, Mechanical Properties of Ceramics Bodies Based on Calcite Waste, Ceramics International, 38 (2012) 8, 6607–6612 R. SOKOLÁØ et al.: INFLUENCE OF CLASS C FLY ASH ON THE PROPERTIES OF PLASTIC CLAY ... Materiali in tehnologije / Materials and technology 54 (2020) 1, 107–111 111