11 KB427 KB10 KB199219991995Crnjak Orel, ZoricaLeskovšek, NevenkaOrel, Borisštevilka:1/2letnik:293 stranistr. 260-262ISSN:1318-0010COBISSID:829978URN:URN:NBN:SI:doc-ZUDSSN6FslInštitut za kovinske materiale in tehnologijeŽelezarna JeseniceŽelezarna RavneŽelezarna ŠtoreKovine zlitine tehnologijepoliesterpremazizamreževanjeŠtudij zamreževanja nasičenega poliestra s heksametoksimetilmelaminom z infrardečo spektroskopijo|Ecological problems, due to the evaporation of organic solvents, are the main reason for application high solid coatings in which binders with lower molecular weight are used. Crosslinking of low molecular weight polymers requires special attentions since greater number of bond must be formed to crosslink the resin binder as in the classical paint systems. The influence of the temperature and catalyst on crosslinking reactions was followed by FTIR spectriscopy in -OH terminated polyester/hexamethoxymethyl melamine clearcoat.The main reaction of transetherification between hydroxy groups on polyester and methoxy groups on melamine was accompanied by several side competative reactionsEkološki problemi pospešujejo uporabo premaznih sredstev z nizko vsebnostjo organskih topil. V tovrstnih premaznih sredstvih se uporabljajo veziva z nizkomolsko maso, pri katerih mora v času zamreževanja nastati več novih vezi,kot pri klasičnih premazih. Cilj raziskave je bil ugotoviti vpliv temperature in količine dodanega katalizatorja na potek zamrežebvanja -OH funkcionalnega poliestra s heksametoksimetil melaminom z uporabo FTIR spektroskopije. Ugotovili smo, da istočasno poteka lahko več reakcij. Poleg transeterifikacije med hidroksi skupinami na poliestru in metoksi skupinami na melaminu, je možnih še več reakcij, ki kompetitivno potekajo ves čas segrevanjaTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije