8 KB430 KB8 KB199219991995Jenko, MonikaSteiner Petrovič, DarjaVodopivec, Francletnik:293 straništevilka:5/6str. 459-461ISSN:1318-0010COBISSID:5546URN:URN:NBN:SI:doc-S98IC9DEslInštitut za kovinske materiale in tehnologijeŽelezarna JeseniceŽelezarna RavneŽelezarna ŠtoreKovine zlitine tehnologijeelektropločevinajeklomikrosrukturarast zrnrekristalizacijaPoprava, rekristalizacija in rast zrn v jeklu z 2% Si - 0,3% Al - 0,003% C| Recovery, recrystallization and grain growth in a 2% Si - 0,3% Al - 0,003% C Steel|The decarburized and undecarburized cold rolled electrical steels were annealed in a deoxidized lead bath in the temperature range from 550 to 800°C. The microstructure was examined and the average grain size assesed. The process of recovery was investigated on specimens annealed at lower temperatures by hardness measurements. Industrially manufactured samples of non-oriented sheets were used as comparisonVzorce razogljičene in nerazogljičene neorientirane elektro pločevine laboratorijske izdelave smo žarili v svinčevi kopeli v temperaturnem območju od 550 do 800°C. Spreminjali smo procese, ki v deformiranih kovinah potekajo med žarjenjem - popravo, rekristalizacijo in rastjo rekristaliziranih zrn. Izmerili smo trdoto vzorcev, ki smo jih žarili pri temperaturah, ko poteka poprava. Na podlagi mikrostruktur smo spremljali nastanek rekristalizacijskih kali, ocenili velikost zrn in določili kinetiko rekristalizacije. Industrijsko izdelano jeklo je rabilo v primerjalne nameneTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije