12 KB60 KB12 KB199219991998Pihura, Dervišletnik:32številka:6str. 567-569ISSN:1318-0010COBISSID:95402URN:URN:NBN:SI:doc-NFXKXVWZenInštitut za kovinske materiale in tehnologijeŽelezarna JeseniceŽelezarna RavneŽelezarna ŠtoreKovine zlitine tehnologijegrodeljmanganoblogeognjevzdržni materialižlindraInfluence of higher manganese content in hot metal on lining| Vpliv večje vsebnosti mangana v grodlju na oblogo|Metallic charging materials, with higher manganese content (up to 4%) show a deleterious influence on the lining of the melting shop equipment. Manganese from hot metal or manganese oxide from slag reacts with CaO and MgO from dolomite refraactory lining forming different oxide compounds. MnO acts as solutant and catalizator of some processes. In this way dolomite lining or bricks are destroyedTekoči grodelj z zvišanim manganom (do 4%) negataivno vpliva na ognjevzdržno obzidavo talilnih agregatov za izdelavo jekla in zmanjšuje življensko dobo teh agregatov. Mangan ali oksid mangana v žlindri reagira s CaO in MgO iz dolomitne obloge. MnO deluje kot topilo in katalizator različnih procesov. Na ta način se ognjevzdržna obloga in opeka razkrajata in razpadata. Razpad ognjevzdržnega materiala je predvsem posledica kemičnih reakcij med MnO in ognjevzdržnim materialom. Zaradi tega so nujni ukrepi za pripravo tekočega grodljaNadaljuje se kot: Materiali in tehnologijeTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije