13 KB726 KB12 KB199219991995Mirtič, Bredaletnik:295 straništevilka:5/6str. 475-479ISSN:1318-0010COBISSID:1630URN:URN:NBN:SI:doc-MEMH25Z6slInštitut za kovinske materiale in tehnologijeŽelezarna JeseniceŽelezarna RavneŽelezarna ŠtoreKovine zlitine tehnologijedifuzijagradivakromitno magnezitno gradivoDifuzija železovih ionov v kromitno magnezitnih gradivih|Magnesia-chrome refractories decay because of differenc causes. Some damaging appearances have been already investigated. The present article describes the causes and kinds of iron diffusion into periclase and chromate aggregates which compose the magnesia-chrome refractory and formation of magnesium ferrite. Inversely, magnesium wustite is formed during iron diffusion out of periclase aggregates. Reactions depend on temperature, quantitz of iron and partial oxygen pressure in kiln. Magnesium ferrite and wustite formation influence the refractory brick porosity and consecutively its strength and mechanical resistanceKromitno magnezitna gradiva propadajo na mestu gradnje zaradi različnih vzrokov, ki so jim tam izopistavljena. Nekateri pojavi propadanja so bili že raziskani. V predstavljenem delu so opisani vzroki in načini difuzije železovega iona v agregate periklaza in kromita, iz katerih je sestavljena kromitno magnezitno gradivo, ter nastanek magnezijevega ferita oz. magnezijevega wustita pri obrnjeni smeri difuzije železovih ionov iz periklaznega agregata. Reakcije so odvisne od temperature, količine železovih ionov in od atmosfere v peči. Dokazali smo jih z optično in elektronsko mikroskopijo. Nastala magnezijev ferit in magnezijev wustit vplivata na poroznost gradiva, posledično pa na njegovo trdnost in mehansko odpornostTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije