14 KB418 KB12 KB199219991999Bukovec, PeterCerc Korošec, RomanaSorce, GerryŽupanc Mežnar, Leaštevilka:3/4letnik:334 stranistr. 219-222ISSN:1318-0010COBISSID:157354URN:URN:NBN:SI:doc-KGHB5D9CslInštitut za kovinske materiale in tehnologijeŽelezarna JeseniceŽelezarna RavneŽelezarna ŠtoreKovine zlitine tehnologijeevropijkarakterizacijaluminiscenčne spojinesilicijev dioksidsol-gel postopkiAlkoksidna sol-gel sinteza in luminiscenčne lastnosti SiOspodaj2:Eu| Alkoxide sol-gel synthesis and luminescent properties of SiOsub2:Eu|Silica doped with europium (?$SiO_2$?:Eu) was prepared by alkoxide sol-gel method using tetraethoxysilane (TEOS) and europium(III) chloride precursors. ?$SiO_2$? monoliths and powders doped with 1-5 mol % Eu were synthesized and compared with undoped ones. The transmission of transparent monolites was measured in UV-visible region. The heating process, which is the final stage in the preparation of powder, was strudied by thermal analyses. The ?$Eu^{3+}$? transitions were determined with fluorescence spectroscopyZ alkoksidnim sol-gel postopkom smo pripravili nedopiran in z evropijem dopiran silicijev dioksid (?$SiO_2$?:Eu). Kot prekurzorja smo uporabili tetraetilortosilikat (TEOS) in evropijev(III)klorid. ?$SiO_2$? dopiran z 1 in 5 mol % Eu smo sintetizirali v obliki monolitov in prahov in vzorce primerjali z nedopiranimi. Pri prozornih monolitih smo izmerili transmisijo v UV-vidnem področju. S termično analizo smo preučili segrevalni del priprave prahov. S fluorescenčno spektroskopijo smo določili posamezne prehode trivalentnega evropijaTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije