20 KB846 KB18 KB199219991995Vodopivec, Francštevilka:1/2letnik:296 stranistr. 31-36ISSN:1318-0010COBISSID:17100805URN:URN:NBN:SI:doc-IBHNKJODslInštitut za kovinske materiale in tehnologijeŽelezarna JeseniceŽelezarna RavneŽelezarna ŠtoreKovine zlitine tehnologijeduktilnostmagnetne lastnostiMetallurgical and Materials Engineeringmetalurgijamikrostrukturazlitineželezove zlitineMikrostruktura, duktilnost in spinodalno razmešanje v zlitinah Fe28Cr10-16Co|In spite of relatively simple basic composition technical iron-chromium-cobalt alloys for permanent magnets are a complex material. Only with a careful control of impurities and the addition of secondary alloy elements the formation of phases ?$\gamma$? and ?$\sigma$? is prevented and a microstructure of ferromagnetic phase ?$\alpha$? is obtained. A proper combination of thermal treatment for spinodal decomposition and a wire drawing deformation producing magnetic anisotrophy gives the best magnetic properties. The alloys are brittle by room temperature and the deformation is performed at increased temperature, where twinning is replaced by shearing deformationKljub razmeroma enostavni osnovni sestavi so tehnične zlitine železa, kroma in kobalta za permanentne magnete kompleksen material. V njih je mogoče le s kontrolo nečistoč in dodatkom sekundarnih legirnih elementov preprečiti nastanek ?$\gamma$? in ?$\sigma$? faze in doseči mikrostrukturo iz faze ?$\alpha$?, ki omogoča doseganje magnetnih lastnosti. Toplotna obdelava daje najbolj primerno spinodalno strukturo, ustvari najboljšo duktilnost, z vlečenjem pa se ustvari magnetna anizotropija in izboljšajo se magnetne lastnosti. Zlitine so pri temperaturi ambienta krhke, deformacija z vlečenjem je mogoča le pri povišani temperaturi, kjer drsenje zamenja dvojčenjeTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije