12 KB196 KB10 KB199219991998Arzenšek, BorisSkobir, DanijelaVodopivec, Francštevilka:3/4letnik:32str. 177-180ISSN:1318-0010COBISSID:50858URN:URN:NBN:SI:doc-HEVVC5VHslInštitut za kovinske materiale in tehnologijeŽelezarna JeseniceŽelezarna RavneŽelezarna ŠtoreKovine zlitine tehnologijecevijeklomikrostrukturatrdotaVpliv toplotne obdelave na mikrostrukturo in trdoto jekla X20CrMoV121| The influence of heat treatment on microstructure and hardness of X20CrMoV121 steel|From the results of the researches on the pipes, cuted our of the steam boiler of 325 MW TE Šoštanj, it was established that the deformation resistance, after 100 hours staatical load creep at temperature 580°C, was four times lower at the flame side, as at the chimney side. In that research we want to define, if the reason for this distinctive change in deformation abilities is in change of dislocation, submicrostructure, originated at heat treatment of the pipes, or in different conditions of formations molibdenium and vanadium carbides in the steelRaziskave na ceveh, ki so bile izrezane iz temperaturo najbolj obremenjenega dela v 325 MW parnem kotlu TE Šoštanj, so pokazale, da je v ceveh , premera 40 mm, izdelanih iz jekla vrste X20CrMoV121, deformacijska odpornost pri 100-urni statični obremenitvi pri temperaaturi 580°C štirikrat manjša na plamenski kot na dimni strani cevi. V tej raziskavi želimo opredeliti, ali je vzrok za zelo izrazito spremembo deformacijske sposobnosti v podstrukturi, ki je rezultat preureditve dislokacijske podstrukture, nastale pri toplotni obdelavi cevi, ali pa mogoče tudi v tem, da na enem delu cevi nastajajo počasneje izločki obstojnejših karbidov molibdena in vanadijaNadaljuje se kot: Materiali in tehnologijeTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije