8 KB347 KB7 KB199219991995Praček, BorutZalar, AntonZupan, Klementinaštevilka:1/2letnik:293 stranistr. 342-344ISSN:1318-0010COBISSID:17063429URN:URN:NBN:SI:doc-H6317DPQslInštitut za kovinske materiale in tehnologijeŽelezarna JeseniceŽelezarna RavneŽelezarna ŠtoreKovine zlitine tehnologijechemistrykemijamaghemitsintezaželezovi oksidiPreiskava železo-oksidnih magnetnih prahov z metodo AES|Iron-oxide magnetic powders were prepared by thermal treatment of gels obtained in sol-gel procedure. The gels in the form of 1 cm thick layers were annealed in a tube furnace at 370°C for 3 hours. The type of an iron oxide and impurities distribution in final product were determined using AES (Auger Electron Spectroscopy)Železo-oksidne magnetne prahove smo pripravili s termično obdelavo gelov, sintetiziranih po sol-gel postopku (ob dodatku dopantov bora ter cinka). Termična obdelava je potekala v 1 cm debeli plasti v cevni peči, pri temperaturi 370°C na zraku. Z metodo AES (Augerjeva elektronska spektroskopija) smo ugotavljali tip železovega oksida, ki pri termični obdelavi nastaja, porazdelitev dopantov ter nečistoč v končnem produktuTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije