16 KB665 KB14 KB199219991993Koroušić, Blaženkoletnik:27številka:45 stranistr. 313-318ISSN:1318-0010COBISSID:17096965URN:URN:NBN:SI:doc-5OZ33RV4enInštitut za kovinske materiale in tehnologijeŽelezarna JeseniceŽelezarna RavneŽelezarna ŠtoreKovine zlitine tehnologijealuminatni vključkiGibbsov modeljeklaračunalniško vodenjesimulacijetermodinamični modelPredicting oxide activities in CaO-Alsub2Osub3-SiOsub2 system by computer model|The most important metallurgical effects of ladle treatment of aluminium - killed steels with calcium, are associated with the modification of aluminia inclusions. For the development of the deoxidation - controled model for inclusions, the thermodynamic slag model, based on the Gibbs energy minimization and modelling approaches postulated from Hastie et al., was used to calculate component oxide activities in the system CaO.Alsub2 Osub3-SiOsub2, 12CaO.7Alsub2 Osub3-SiOsub2 and CaO.Alsub2 Osub3-SiOsub2 at 1500°C and 1600°CNajpomembnejši metalurški učinki pri uporabi kalcija za obdelavo jekel, pomirjenih z aluminijem so povezani z modifikacijo aluminatnih vključkov. Pri razvoju modela za kontrolo vključkov smo uporabili termodinamični model, ki sloni na Gibbsovem modelu minimizacije energije in postolatu, ki ga je postavil Hastie et al. Izračubnavanje aktivnosti oksidnih komponent smo izvršili za sistem CaO.Alspodaj2Ospodaj3, 12CaO.tAlspodaj2Ospodaj3-SiOspodaj2 in CaO.Alspodaj2Ospodaj3-SiOspodaj2 pri temperaturi 1500°C in 1600°CTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of Slovenia