14 KB105 KB12 KB199219991998Gontarev, VasilijGrabke, Hans JürgenJenko, MonikaSteiner Petrovič, Darjaletnik:32številka:6str. 493-496ISSN:1318-0010COBISSID:91818URN:URN:NBN:SI:doc-1JDKI1NMenInštitut za kovinske materiale in tehnologijeŽelezarna JeseniceŽelezarna RavneŽelezarna ŠtoreKovine zlitine tehnologijealuminijAluminij MostaraluminumantimonantimonyjeklaoksidacijarazogljičenjesilicijDecarburization mechanism of Fe-Si-Al alloy with antimony addition| Mehanizem razogličenja zlitine Fe-Si-Al, legirane z antimonom|The mechanism of decarburization process of Fe-Si-Al alloy was investigated onsamples of cold rolled sheets; some of them alloyed with 0.048 wt.% Sb. The decarburization was performed in a ?$H_2H_2O$? gas mixture at 840°C. It was influenced by the oxidation of the surface. Antimony influence of on decarburization mechanism of Fe-Si-Al alloy depends on carbon content in the steelRaziskali smo proces razogljičenja vzorcev Fe-Si-Al zlitin v obliki hladno valjane pločevine, ki smo jo legirali z 0,048 mas.% Sb. Razogljičenje je potekalo v atmosferi vlažnega vodika pri temperaturi 840°C. Na kinetiko razogljičenja vpliva tudi oksidacija površine jekla. Vpliv antimona na mehanizem razogljičenja zlitine Fe-Si-Al je bil povezan s koncentracijo ogljika v jekluNadaljuje se kot: Materiali in tehnologijeTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije