24 KB370 KB21 KB200020242010Balać, IgorBojić, KatarinaJančić, Radmila HeinemannProkić-Cvetković, RadicaSedmak, AleksandarTadić, Srdjanletnik:44številka:6str. 357-361ISSN:1580-2949COBISSID:842410URN:URN:NBN:SI:doc-XUPFD1K2enInštitut za kovinske materiale in tehnologijeMateriali in tehnologijedeformacijadrsenjeintermetalne zlitineprelomtitanove zlitineDeformation mechanisms in Ti3Al-Nb alloy at elevated temperatures| Mehanizem deformacije v zlitini Ti3Al-Nb pri povišanih temperaturah|Ti3Al-11Nb-1V (x/%) was made in a vacuum arc furnace. Hot-rolling was conducted at 1050 °C in a two-phase field of the alloy. Strain-rate jump tests were performed at T = 800-1100 °C and strain rates of 10-6 to 10-3 s-1. Creep stress exponent (n) and activation energy for deformation (Q) were used to identify deformation mechanisms. Two sequential mechanisms are revealed: (i) viscous glide, typical of solid solution alloys and, (ii) power law breakdown at lower temperatures. Activation energy for deformation was found to be strongly stress-dependantZlitina Ti3Al-11Nb-1V (x/%) je bila izdelana v vakuumski obločni peči. Vroče valjanje je bilo opravljeno pri 1050 °C v dvofaznem območju zlitine. Sunkoviti preizkusi hitrosti deformacije so bili narejeni pri T = 800-1100 °C in pri hitrosti deformacije 10-6 to 10-3 s-1. Eksponent napetosti lezenja (n) in aktivacijska energija deformacije (Q) sta bila uporabljena za identifikacijo mehanizma deformacije. Odkrita sta bila dva sekvenčna mehanizma: (i) viskozno drsenje, ki je značilno za zlitine iz trdnih raztopin in (ii) prelom potenčnega zakona pri nižji temperaturi. Ugotovljeno je bilo, da je aktivacijska energija deformacije zelo odvisna od napetostiTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije