22 KB428 KB21 KB200020242007Gliha, VladimirVuherer, Tomažštevilka:3letnik:416 stranistr. 125-130COBISSID:11446550ISSN:1580-2949URN:URN:NBN:SI:doc-X2YP8F3IenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijejeklonapakenapetostipriskava materialarazpoketrdnostzvariThe behaviour of coarse-grain HAZ steel with small defects during cycling loading| Vedenje jekla grobozrnatega TVP z napakami pri ciklični obremenitvi|The effects of small, artificial surface defects on the fatigue strength of coarse grain HAZ material found at the weld toe were studied. The size of defects did not exceed the grain size, which is the most relevant microstructural unit of polycrystalline metals. The artificial defects were made by indenting the material with Vicker`s pyramid and by drilling holes. The samples of coarse-grain HAZ material were prepared using a welding thermal-cycle simulator or furnace. The mexperimentally determined bending fatigue strength versus the properly evaluated defects siye was compared with the propagation of long cracks. Residual stresses appear when making small artificial defects. The crack initiation from the defects was analysed and theinfluence of residual stresses is discussedTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije