19 KB1129 KB16 KB200020262013Bhattacharya, BhaskarSachdeva, AmitSingh, Pramod K.Singh, Rojaštevilka:4letnik:47str. 467-471COBISSID:1004202ISSN:1580-2949URN:URN:NBN:SI:doc-WXZD4FBMenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijekalijev galunkompozitipepelpreiskava materialaprevodnostSynthesis, characterization and sensing application of a solid alum/fly ash composite electrolyte| Sinteza, karakterizacija in možnost uporabe trdnega kompozitnega elektrolita galun-leteči pepel|A new composite system using low-cost materials, potash alum and fly ash, was prepared and characterized using various techniques. Complex impedance spectroscopy was used for the conductivity measurement. A conductivity enhancement due to an addition of fly ash was observed and the maximum value was obtained with the 65 : 35 compositions. The maxima in conductivity can be explained with the percolation theory. Infrared spectroscopy (IR) as well as X-ray diffraction (XRD) confirmed the composite nature of the samples. Scanning electron microscopy (SEM) shows a good homogeneous mixture of the composite material which is essential for the conductivity enhancement. Based on the maximum-conductivity composition, a humidity sensor was fabricated which showed a good sensing behaviorPripravljen in karakteriziran z različnimi tehnikami je bil nov kompozitni sistem iz poceni kalijevega galuna in letečega pepela. Za meritve prevodnosti je bila uporabljena kompleksna impedančna spektroskopija. Opaženo je bilo maksimalno povečanje prevodnosti zaradi dodatka letečega pepela pri razmerju sestave 65 : 35. Maksimum prevodnosti lahko razložimo s teorijo pronicanja. Infrardeča spektroskopija (IR) in rentgenska difrakcija (XRD) sta potrdili kompozitno osnovo vzorcev. Vrstična elektronska mikroskopija (SEM) je pokazala homogeno mešanico kompozitnih materialov, ki je ključna za povečanje prevodnosti. Na osnovi sestave z največjo prevodnostjo je bil izdelan senzor vlage, ki je pokazal dobro občutljivostTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije