31 KB633 KB23 KB200020242012Babic, JasminaBajić, DarkoMilosavljević, AndjelkaPetronić, SanjaPolic-Radovanovic, Suzanaštevilka:4letnik:46str. 411-417ISSN:1580-2949COBISSID:938922URN:URN:NBN:SI:doc-WTZUX9MRenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijeEDSheat-treatmentmicrostructuremikrostrukturarentgenska disperzijska spektroskopijaSEMsuperalloysuperzlitinatoplotna obdelavavrstična elektronska mikroskopijaThe influence of the heat-treatment regime on a fracture surface of nickel-based supperalloys| Vpliv toplotne obdelave na površino preloma superzlitin na osnovi niklja|Nickel-based superalloys are distinguished from other materials by their excellent mechanical and physical properties. As they are used at high temperatures and pressures, as well as in aggressive environments, their characteristics need constant improvement. An adequate choice of their chemical composition and the heat-treatment regime contributes to the improvement of the chemical, physical and mechanical properties of these nickel-based superalloy materials. During the heat treatments of the superalloys Nimonic 263 and Hastelloy S some changes in their microstructures were observed. In this paper the changes in the microstructures after various regimes of the heat treatment were analysed on the fractured surfaces. The fractured surfaces were observed using light microscopy, scanning electron microscopy (SEM), and energy-dispersive X-ray spectrometry (EDS)Superzlitine na osnovi niklja se razlikujejo od drugih materialov zaradi svojih odličnih mehanskih in fizikalnih lastnosti. Ker se jih uporablja pri visokih temperaturah in tlakih ter v agresivnem okolju, je potrebno stalno izboljševati njihove lastnosti. Primerna izbira kemijske sestave in načina toplotne obdelave prispevata k izboljšanju kemijskih, fizikalnih in mehanskih lastnosti superzlitine na osnovi niklja. Med toplotno obdelavo superzlitine Nimonic 263 in Hastelloy S se opazijo spremembe v mikrostrukturi. V tem članku so analizirane spremembe mikrostrukture na prelomnih površinah po različnih toplotnih obdelavah. Površina prelomov je bila opazovana s svetlobno mikroskopijo, vrstično elektronsko mikroskopijo (SEM) in rentgensko disperzijsko spektroskopijo (EDS)TEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije