19 KB293 KB18 KB200020242001Grabke, Hans J.Jenko, MonikaPrešern, VasilijSteiner Petrovič, Darjaletnik:355 straništevilka:6str. 337-341ISSN:1580-2949COBISSID:328031URN:URN:NBN:SI:doc-VIT8XGGNenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijeelektropločevinarazogljičenjerekristalizacijaselenvključkiDecarburization of non-oriented electrical steel sheets doped with selenium| Razogljičenje neorientirane elektropločevine, legirane s selenom|Gas-metal reactions like decarburization annealing are affected by the temperature, the composition of the metal surface and the gas mixture. During annealing, interactions take place among the atoms on the steel's surface, those from the gas phase, as well as dissolved atoms from the bulk and segregated atoms. Several authors have reported that selenium improves the magnetic properties of grain-oriented electrical steel sheets. The effect of 0,05 mas. % of Se on the decarburization of non-oriented silicon steel sheet has been investigated in this studyKemijske reakcije na fazni meji plin-kovina, npr. razogljičenje, so odvisne od temperature, kemijske sestave kovinske površine in plinske mešanice. Na površini jekla med žarjenjem nastajajo interakcije med atomi iz plinske faze, raztopljenimi atomi iz trdne raztopine in segregiranimi atomi iz jekla. Različni raziskovalci poročajo, da selen izboljšuje magnetne lastnosti orientiranih elektropločevin. V tej raziskavi smo preučevali vpliv 0,05 mas. % Se na razogljičenje neorientirane elektropločevineTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije