18 KB985 KB17 KB200020262001Križman, AlojzOhata, MitsuruPraunseis, ZdravkoToyoda, Masaoštevilka:3/4letnik:356 stranistr. 161-166ISSN:1580-2949COBISSID:6474774URN:URN:NBN:SI:doc-VHQHHWSTenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijefazekonstrukcijske jeklamikrostrukturanizko legirano jeklovarjenjevisokotrdnostna jeklazvariVloga in nastanek mikrostrukturnih sestavin M-A v zvarnih spojih maloogljičnih visokotrdnostnih konstrukcijskih jekel| The role and formation of martensite-austenite constituents in HSLA welded joints|The existence of martensite-austenite constituents in the weld metal and heat-affected zone seriously reduces the fracture toughness of the welded joint. Therefore, we have investigated the formation of the martensite-austenite constituents when high-strength low-alloy steel is welded with a high heat input or using multi-pass welding. This paper deals with the effects of martensite-austenite constituents on the fracture toughness, the metallurgical features of the martensite-austenite constituents, and the prevention and elimination of the martensite-austenite constituents in the welded jointsMartenzitno-avstenitne sestavine v varu in na toplotno vplivanem področju drastično zmanjšujejo lomno žilavost zvara. Zaradi tega je treba posebno pozornost nameniti nastanku teh sestavin pri večvarkovnem varjenju visokotrdnostnih jekel z visoko vneseno energijo. V članku je opisan vpliv martenzitno-avstenitnih sestavin na lomno žilavost, metalurške značilnosti le-teh ter njihovo preprečevanje in odpravljanje v zvarihTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije