URN:NBN:SI:DOC-UW04RSK82026Chen, GuanlinChen, JinfengChu, ZhibingHou, XiansheHu, YijianHuang, Xian’anLi, GuifengQiao, Ziruidocuments/doc/U/URN_NBN_SI_doc-UW04RSK8_001.pdfdocuments/doc/U/URN_NBN_SI_doc-UW04RSK8_001.txt560articlestr. 745–75910.17222/mit.2026.17791580-2949301060099URN:NBN:SI:doc-UW04RSK8engInštitut za kovinske materiale in tehnologijeMateriali in tehnologijeBY316L seamless tubesbrezšivne cevifinite-element simulationmicrostructure evolutionneprekinjeno valjanje s tremi valji in trnomnerjavno jeklo tipa 316Lrazvoj mikrostruktursimulacija z metodo končnih elementovthree-roll retained mandrel continuous rollingThe effect of rolling speed and reduction amount on the stress strain field and microstructural evolution of 316L stainless steel tubes during hot continuous rollingVpliv hitrosti in stopnje redukcije kontinuirnega vročega valjanja nerjavnega jekla tipa 316L za brezšivne cevi na njegovo napetostno in deformacijsko polje ter razvoj njegove mikrostrukture