696 KB17 KB200320222008Bradaškja, BoštjanFazarinc, MatevžKnap, MatjažKoruza, JurijTurk, Radomirštevilka:1letnik:55str. 31-40ISSN:1408-7073COBISSID:45520URN:URN:NBN:SI:doc-RKMJJOHRenInštitut za rudarstvo, geotehnologijo in okoljeNaravoslovnotehniška fakultetaRMZ-materials and geoenvironmentGleeblelitjemakrostrukturaohlajevalne krivuljestrjevanjeA laboratory test for simulation of solidification on Gleeble 1500D thermo-mechanical simulator| Laboratorijski test simulacije strjevanja na termo-mehanskem simulatorju Gleeble 1500D| RMZ - Materiali in geookolje|A highly repeatable solidification test was developed. It was designed to study the effect of process parameters on solidified micro and macrostructures. Different cooling rates were used for solidification and cooling of S 355 J2 construction steel. It was observed that cooling rate has a substantial influence on final grain size and on columnar-to-equiaxed transition zone (CET). Within the interval of constant thermal gradient, different macro- and micro-structural features have been provided, which consequently enables the study of dynamics of precipitation dependence on solidification processing parametersRazvit je bil visoko ponovljiv test strjevanja. Razvit je bil kot orodje za preučevanje vpliva procesnih parametrov na lito mikro in makrostrukturo. Za strjevanje konstrukcijskega jekla S 355 J2 so bile uporabljene različne ohlajevalne hitrosti. Opažen je bil močan vpliv ohlajevalne hitrosti tako na končno velikost zrn, kot tudi na mejno plast med stebričastimi in ekviaksialnimi zrni. Znotraj intervala, kjer je bil temperaturni gradient konstanten, so bile s pomočjo različnih ohlajevalnih hitrosti, v vzorcih dobljene različne mikro in makrostrukturne značilnosti, kar omogoča študij dinamike izločanja v odvisnosti od parametrov strjevanjaTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaUniverza v Ljubljani, Naravoslovnotehniška fakulteta