24 KB392 KB18 KB200020242010Hájková, PavlínaJanovec, JiříSiegl, JanSmola, BohumilTůmová, DanielaVyroubalová, Michaelaštevilka:4letnik:44str. 227-232ISSN:1580-2949COBISSID:821674URN:URN:NBN:SI:doc-RIHMTJZBenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijeferitlegirana jeklalopaticemikrostrukturaturbineutrujenost materialovInfluence of delta-ferrite on the fatigue resistance of blade materials| Vpliv delta-ferita na utrujenostno trdnost jekel za lopatice|The low-pressure parts of a TG 1000 MW turbine, for the third wheels, are made from modified 12 % Cr martensitic steel AK1 TD.9, and the fourth, are madefrom X2CrNiMo13-4 steel. The fracture of the third turbine wheel at the point of the connection part of the blade has a high-cycle fatigue character with multiple initiation sites. An analysis of the microstructure has proved the influence of both the delta-ferrite content and the arrangement on the initiation point of the fatigue process. Also, an inspection of the fatigue crack's kinetics in relationship to the operating mode of the power plant has been carried outNizkotlačni deli turbine TG 1000 MW iz tretjega venca so iz modificiranega 12-odstotnega Cr martenzitnega jekla AK TF.9, iz četrtega venca pa iz jekla X2CrNiMo 13-4. Prelom tretjega turbinskega venca v točki vpetja ima značaj visoke ciklične utrujenosti z mnogimi začetnimi mesti. Analiza mikrostrukture je pokazala vpliv vsebine in porazdelitve delta-ferita na začetno točko procesa utrujenosti. Ugotovljena je bila tudi povezava kinetike utrujenostne razpoke značinom dela turbineTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije