918 KB17 KB201320252015Mlakar, MarkoNovak, SonjaPraunseis, Zdravkoletnik:8številka:iss. 4str. 11-22COBISSID:1024224348ISSN:1855-5748URN:URN:NBN:SI:doc-REQTPU1PenFakulteta za energetikoJET on-lineJournal of energy technologycrack frontdipolesteel weldsfracture toughnessheat-affected zonejeklorazpokezvarizvarni spojiDetermination of local brittle zones at the crack front in the HAZ of welded joint| Določitev krhkih področij na fronti razpoke v TVP zvarnega spoja|Welded joints are the weakest link in the construction of steel structures. The brittlest part of a multi-pass welded joint is the heat-affected zone, where brittle fractures of the structure often appear. In this article, examination of the whole heat-affected zone of high strength multipass X welded joints was performed. All microstructures and the local brittle zones% sizes at the crack tip front were precisely determinedZvarni spoji so pri gradnji energetskih komponent najšibkejši člen jeklene konstrukcije. Najbolj krhko področje večvarkovnega zvarnega spoja je toplotno vplivano področje, kjer se najpogosteje pojavi krhki zlom konstrukcije. V članku je obravnavano celotno toplotno vplivano področje visokotrdnostnega večvarkovnega X zvarnega spoja. Natančno so določene vse krhke mikrostrukture in velikosti lokalno krhki področij ob fronti utrujenostne razpokeTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaUniverza v Mariboru, Fakulteta za energetiko