138 KB19 KB200020242014Jenko, MonikaPodgornik, BojanVodopivec, FrancŽužek, Borutštevilka:4letnik:48str. 545-548COBISSID:1068202ISSN:1580-2949URN:URN:NBN:SI:doc-QO0OSXYAenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijecoarseningcreep ratescreep-resistant steeldissolutionhitrost lezenjaizločkijeklolezenjeparticlesrastraztapljanjetemperature effectvpliv temperatureEffect of creep strain on creep rate in the temperature range 550-640 °C| Vpliv deformacije na hitrost lezenja pri temperaturah od 550 °C do 640 °C|Experimental and calculated creep rates were examined for a high-chromium, creep-resistant steel samples quenched and tempered for 2 h and 400 h at 800 °C. Creep testing and annealing were carried out at 550 °C to 640 °C. It was found that the difference in the creep rates due to the particle coarsening and dissolution was independent of the temperature, while the ratio of the experimental and calculated creep rates increased with the temperature of the creep tests. The results suggest that an increase in the creep rate is related to the process of vacancy climb in parallel with the increase in the diffusion rate of the iron in the ferriteHitrost lezenja je bila eksperimentalno določena in izračunana za jeklo, odporno proti lezenju, z visoko vsebnostjo kroma pri vzorcih, ki so bili kaljeni in popuščani 2 h oz. 400 h pri 800 °C. Stourni preizkusi lezenja in žarjenja so bili izvršeni pri 550 °C do 640 °C. Razlika v hitrosti lezenja zaradi raztapljanja oziroma rasti izločkov je bila neodvisna od temperature, medtem ko je razlika med eksperimentalno in izračunano hitrostjo lezenja večja pri višji temperaturi. Rezultati meritev in izračunov kažejo, da je povečanje hitrosti lezenja povezano z večjo hitrostjo plezanja vrzeli, ki je vzporedno s povečanjem hitrosti difuzije železa v ferituTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije