18 KB202 KB17 KB200020262000Gliha, VladimirUle, BorisVojvodič-Tuma, JelenaVuherer, Tomažletnik:344 straništevilka:6str. 371-374ISSN:1580-2949COBISSID:210783URN:URN:NBN:SI:doc-PFXBLHLQslInštitut za kovinske materiale in tehnologijeMateriali in tehnologijekonstrukcijska jeklalomna žilavostzvariPrimerjava lomne žilavosti TVP, izmerjene pri dveh vrstah majhnih preizkušancev| Comparison of HAZ fracture toughness measured by two types of small scale specimens|Samples of material with microstructures of four different HAZ situated at the fusion line were prepared on a Gleeble simulator. Specimens for the experimental determination of impact and fracture toughness were machined from samples. The fracture toughness was measured on two types of small pre-cracked specimens. The ?$K_{Ic}$? was determined on round tensile specimens while the ?$\theta_{c}$? was obtained from SENB specimens. The results obtained from the SENB specimens are too optimistic in comparison with the ?$K_{Ic}$?. The SENB specimens are not thick enough, even at very low fracture toughnessNa simulatorju Gleeble smo pripravili vzorce materiala z mikrostrukturo štirih različnih TVP ob črti taljenja. Iz njih smo izdelali preizkušance za merjenje udarne in lomne žilavosti. Lomno žilavost smo izmerili pri dveh vrstah majhnih preizkušancev z razpoko: pri okroglih nateznih in upogibnih SENB-preizkušancih. Pri prvih smo lahko določili ?$K_{Ic}$?, pri drugih pa ?$\theta_{c}$?. Ko primerjamo vrednosti ?$\theta_{c}$? s ?$K_{Ic}$?, dobimo preoptimistične rezultate. Debelina SENB-preizkušancev je tudi pri zelo nizki lommni žilavosti še premajhnaTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije