1539 KB9 KB200020262014Demirkiran, Ayse Şükranštevilka:3letnik:48str. 419-421COBISSID:1057962ISSN:1580-2949URN:URN:NBN:SI:doc-ODMLJISFenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijeceramicfrictionkeramikaobrabatrenjewearzeolitzeoliteWear properties of ceramic bodies produced with natural zeolite| Vedenje keramičnih teles, izdelanih iz naravnega zeolita, pri obrabi|In this study, the wear and friction behaviours of a ceramic disk produced from natural zeolite were studied using a ball-on-disk arrangement. Samples were fired in an electric furnace with a heating rate of 10 °C/min at 1150 °C for a period of 60 min. Friction and wear tests were carried out in dry test conditions under the (2.5, 5 and 7.5) N loads at the (0.1, 0.3 and 0.5) m/s sliding speedsV tej študiji je predstavljeno vedenje keramične ploščice, izdelane iz naravnega zeolita, pri obrabi in trenju na napravi krogla na disku. Vzorci so bili žarjeni v električni peči s hitrostjo ogrevanja 10 °C/min, 60 min pri temperaturi 1150 °C. Preizkusi trenja in obrabe so bili izvršeni v suhih razmerah z obremenitvami (2,5, 5 in 7,5) N pri hitrostih drsenja (0,1, 0,3 in 0,5) m/sTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije