410 KB11 KB200020242013Ergin, NuriGarip, YigitOzdemir, Ozkanletnik:47številka:5str. 669-671COBISSID:1022122ISSN:1580-2949URN:URN:NBN:SI:doc-NI9SFLTRenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijealuminijev oksidcompositekompozitoksidacijaoxidationreduction combustion synthesisredukcijska zgorevna sintezasinteringsintranjetitanov boridOxidation of the Al2O3-TiB2 composites produced with the reduction-combustion synthesis technique| Oksidacija kompozita Al2O3-TiB2, izdelanega s tehniko redukcijske zgorevne sinteze|In this study, Al2O3-TiB2 composites were synthesized in an electrical resistance furnace in open atmosphere under the uniaxial pressure of 150 MPa at 1200 °C for 4 h, using the reduction-combustion synthesis technique. The initial powder mixture used in this study is Al+TiO2+B2O3. TiB2, Al2O3 and some trace phases were found in the produced composites using the X-ray diffraction analysis. The densities of the samples were measured using the Archimedes' technique. The relative density was determined as 94.2 % for the composites. The oxidation properties of the composites were examined in open atmosphere at 600 °C, 800 °C and 1000 °C after up to 64 h. The activation energy of the composite was calculated to be 90 kJ/molV tej študiji je bil sintetiziran kompozit Al2O3-TiB2 v električni uporovni peči z normalno atmosfero pri enoosnem tlaku 150 MPa in 4 h pri 1200 °C z uporabo tehnike redukcijske zgorevne sinteze. Začetna mešanica prahov, uporabljena v tej študiji, je bila Al+TiO2+B2O3. Z rentgensko difrakcijo so bili v izdelanem kompozitu odkriti TiB2, Al2O3 in nekaj faz v sledovih. Gostota vzorcev je bila izmerjena z Arhimedovo tehniko. Relativna gostota kompozita je bila 94,2-odstotna. Oksidacijske lastnosti kompozita so bile preiskane na zraku po 64 h na temperaturah 600 °C, 800 °C in 1000 °C. Izračunana aktivacijska energija kompozita je bila 90 kJ/molTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije