179 KB18 KB200020242014Kokošar, JankoNagode, AlešNovak, GašperSteiner Petrovič, Darjaletnik:48številka:6str. 997-1001COBISSID:1109674ISSN:1580-2949URN:URN:NBN:SI:doc-M1CPE93BenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijeanomalne izgubeBertottijev modelBertotti's modelelectrical steelelektropločevineexcess lossrelative permeabilityrelativna permeabilnostSteinmetz equationSteinmetzova enačbaCorrelation between the excess losses and the relative permeability in fully finished non-oriented electrical steels| Korelacija med anomalnimi izgubami in relativno permeabilnostjo v gotovih neorientiranih elektropločevinah|Using the modified Steinmetz equation and Bertotti's model, the correlation between the excess losses and the relative permeability of non-oriented electrical steel was investigated. Three different steel grades were used in the study: M530-50A, M400-50A and M350-50A. It was observed that both the excess losses and the relative permeability increase in the region of the low magnetic flux density; they both reach their peak values at 0.9-1.0 T, and then drop to the minimum values as the electrical steel is magnetized to saturationZ uporabo modificirane Steinmetzove enačbe in Bertottijevega modela smo ugotovili korelacijo med anomalnimi izgubami in relativno permeabilnostjo v neorientiranih elektropločevinah. V raziskavi smo uporabili tri različne kvalitete: M530-50A, M400-50A in M350-50A. Ugotovili smo, da tako vrednosti anomalnih izgub kot tudi relativne permeabilnosti začnejo naraščati v območju majhnih gostot magnetnega pretoka, dosežejo svojo maksimalno vrednost v istem območju (med 0,9 T in 1,0 T) in se nato zmanjšujejo do minimalnih vrednosti, ko je jeklo tudi namagneteno do nasičenjaTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije