13 KB656 KB9 KB200020262011Balcar, MartinBažan, JiříFila, PavelGodec, MatjažMartínek, LudvíkNovák, JaroslavSkobir Balantič, Danijela AnicaSocha, LadislavSochor, Liborletnik:45številka:6str. 619-622ISSN:1580-2949COBISSID:892586URN:URN:NBN:SI:doc-LFKTBTZUenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijeHSLA-jeklokaljenjemikrolegirano jeklomikrostrukturapopuščanjevpliv temperatureHeat treatment and mechanical properties of heavy forgings from A694-F60 steel| Toplotna obdelava in mehanske lastnosti težkih izkovkov iz jekla A694-F60|The production of heavy steel forgings of micro-alloyed steels gives the possibility to obtain advantages associated with the benefit of the application of micro-alloying elements and thermomechanical treatments for improving the mechanical properties of forgings to level by sheets, strips and tubes. The paper presents the influence of quenching temperature on the mechanical properties and microstructure of F60 steel according to ASTM A694. The verification of the influence of quenching temperature contributes to an optimization of the method of micro-alloyed steel heat treatment. The steel's microstructure and mechanical properties after quenching constitute the initial and basic criteria to achieve the required mechanical properties after a properly chosen tempering temperatureProizvodnja težkih izkovkov iz mikrolegiranih jekel omogoča, da se uporabijo prednosti mikrolegiranja in termomehanske obdelave za doseganje mehanskih lastnosti pri trakovih, ploščah in ceveh. V članku je predstavljen vpliv temperature kaljenja na mehanske lastnosti in mikrostrukturo. Preveritev vpliva temperature kaljenja je del procesa opredelitve in optimizacije metode toplotne obdelave mikrolegiranega jekla. Mikrostruktura in mehanske lastnosti po toplotni obdelavi so osnovni pogoj za doseganje predpisanih lastnostiTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije