27 KB762 KB24 KB200020242011Arh, BoštjanArzenšek, BorisPirnar, BoštjanSkobir Balantič, Danijela AnicaTehovnik, FrancŽužek, Borutštevilka:4letnik:45str. 339-345ISSN:1580-2949COBISSID:866474URN:URN:NBN:SI:doc-IUZ4TKL4enInštitut za kovinske materiale in tehnologijeMateriali in tehnologijedupleksno nerjavno jeklomikrostrukturatrdotavroče valjanježarjenjeMicrostructure evolution in SAF 2507 super duplex stainless steel| Razvoj mikrostrukture v superdupleksnem nerjavnem jeklu SAF 2507|The change of microstructure for a super duplex stainless steel SAF 2507 during hot rolling was investigated. Its evolution during hot deformation was very different in each phase. The dominant restoration mechanism for ferrite and austenite were dynamic recovery (DRV) and dynamic recrystallization (DRX), respectively. Also, the effect of temperature on the deleterious phase precipitation was investigated. The specimens were heat treated isothermally in the temperature range 800 compositumC to 1000 compositumC. Hardness tests, and optical and scanning electron microscopy were used to detect the sigma phaseMed vročim valjanjem je bil raziskan mikrostrukturni razvoj v superdupleksnem nerjavnem jeklu SAF 2507, ki se med vročo deformacijo razlikuje v vsaki fazi. Prevladujoč mehanizem mehčanja v feritu in avstenitu je bila dinamična poprava in/ali dinamična rekristalizacija. V superdupleksnem nerjavnem jeklu je bil raziskan vpliv temperature na izločanje škodljivih faz. Vzorci so bili izotermno toplotno obdelani v temperaturnem območju od 800 °C do 1000 °C. Uporabljene so bile meritve trdote ter optična in elektronska mikroskopija za analizo sigma-fazeTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije