26 KB109 KB23 KB200020262011Celin, RomanJenko, MonikaSkobir Balantič, Danijela AnicaVodopivec, FrancŽužek, Borutštevilka:2letnik:45str. 139-143ISSN:1580-2949COBISSID:856746URN:URN:NBN:SI:doc-HCDINAKBenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijejeklolezenjemikrostrukturazvariCreep resistance of microstructure of welds of creep resistant steels| Odpornost proti lezenju pri mikrostrukturi zvarov jekel, odpornih proti lezenju|Welds are essential parts of tube systems in high temperature power works producing electricaql energy and have a heterogeneus microstructure due to the welding gradient of temperature and cooling rate. A short summary is given of findings related to the creep resistance of welds of creep resistant steels. In the majority of references it was found that creep resistance was lower for the intercritical part of heat affected zone (HAZ). The effect of potential changes of intercritical microstructure on creep rate at exploitation is discusedZvari so bistvena komponenta cevnih sistemov v termoelektrarnah, njihova mikrostruktura pa je heterogena zaradi gradienta temperature in ohlajanja pri varjenju. Pripravljen je bil kratek pregled ugotovitev v zvezi z odpornostjo različnih delov cone toplotnega vpliva varjenja (TVC) proti lezenju v dosegljivih virih. Večina virov navaja, da je odpornost najnižja v področju, kjer je bilo med varjenjem jeklo segreto v interkritično področje CTV. Analizirane so mogoče spremembe interkritične mikrostrukture in od njih odvisne spremembe hitrosti lezenjaTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije