27 KB955 KB25 KB200020242011Skobir Balantič, Danijela Anicaštevilka:4letnik:45str. 295-301ISSN:1580-2949COBISSID:865450URN:URN:NBN:SI:doc-H7KGEVARenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijekarbidikarbonitridimalolegirana jeklamehanske lastnostimikrolegirana jeklanitridiHigh-strength low-alloy (HSLA) steels| Visokotrdna malolegirana (HSLA) konstrukcijska jekla|Micro-alloyed, high-strength, low-alloy (HSLA) steels are important structural materials and contain small amounts of alloying elements, such as niobium, titanium, vanadium, and aluminium, which enhance the strength through the formation of stable carbides, nitrides or carbonitrides and have an effect on the hardenability. Such steels contain less than 0.1 % of the alloying additions, used individually or in combination. Yield strength increments of two or three times that of plain carbon-manganese steel can be attained. Nowadays, also micro-alloyed cast steels have found many applications in the manufacturing of industrial parts that used to be produced by more expensive manufacturing processesVisokotrdna malolegirana konstrukcijska jekla (HSLA) spadajo med tehnično pomembne konstrukcijske materiale in vsebujejo majhne količine legirnih elementov, kot so niobij, titan, vanadij, aluminij, ki zaradi tvorbe stabilnih karbidov, nitridov ali karbonitridov zvišajo natezno trdnost materiala in vplivajo na trdnost. Ta jekla vsebujejo manj kot 0.1 % legirnih elementov, ki se lahko uporabljajo posamezno ali v kombinaciji, natezna trdnost pa je lahko dva do trikrat višja kot pri navadnem ogljikovo-manganovem jeklu. Danes so v uporabi tudi mikrolegirana lita jekla, ki se največ uporabljajo za izdelavo raznih industrijskih delov, za kar so bili prej potrebni dragi proizvodni procesiTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije