23 KB680 KB20 KB200020242012Fu, GaoshengYan, Wenduanletnik:46številka:6str. 637-642ISSN:1580-2949COBISSID:956842URN:URN:NBN:SI:doc-GOIP0MJEenInštitut za kovinske materiale in tehnologijeMateriali in tehnologije1235 aluminium alloyaluminijeve zlitinealuminium alloydynamic recrystalizationhot deformationprocessing maprekristalizacijavroče preoblikovanjeDetermining the hot-deformation characteristics of A 1235 aluminum alloy using a processing map| Značilnosti vroče deformacije aluminijeve zlitine 1235 z uporabo načrta procesiranja|A hot-processing map and TEM images of a 1235 aluminum alloy have been used while studying hot-deformation characteristics of this alloy. The results showed that an ideal processing region exists in the high-temperature/low-strain-rate area and that the power-dissipation efficiency is around 46 %. It is better to avoid deformations at the low-tempera- ture/high-strain rate and the high-temperature/moderate-strain rate due to their processing instability and lower power-dissipation efficiencyNačrt vročega preoblikovanja in TEM-posnetki aluminijeve zlitine 1235 so bili uporabljeni pri študiju značilnosti preoblikovanja v vročem aluminijeve zlitine 1235. Rezultati so pokazali, da obstaja idealno področje preoblikovanja v območju visoke temperature - majhne preoblikovalne hitrosti in z okrog 46 % izgube efektivne moči. Boljše se je izogibati preoblikovanju pri nizkih temperaturah - velikih preoblikovalnih hitrostih in pri visokih temperaturah - zmernih preoblikovalnih hitrostih zaradi nestabilnosti preoblikovanja in manjše učinkovitosti izgubljene močiTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije