URN:NBN:SI:DOC-G6KQBJQG2024Chu, ZhibingGui, HailianJin, RiLi, TuoLi, YuquanMa, ChuanchuanTuo, LeifengXue, Chundocuments/doc/G/URN_NBN_SI_doc-G6KQBJQG_001.pdfdocuments/doc/G/URN_NBN_SI_doc-G6KQBJQG_001.txt586articlestr. 699–70610.17222/mit.2024.12151580-2949219600387URN:NBN:SI:doc-G6KQBJQGengInštitut za kovinske materiale in tehnologijeMateriali in tehnologijeInCcrystal structuredislocation line densitykristalna strukturalinijska gostota dislokacijloading directionmagnesium single crystalmolecular dynamicsmolekularna dinamikamono kristali magnezijasmeri obremenjevanjaEffects of different loading directions on the organization and properties of magnesium single crystals based on molecular dynamicsAnaliza vplivov različnih smeri obremenjevanja na organizacijo in lastnosti magnezijevih monokristalov s pomočjo molekularne dinamike