13 KB121 KB12 KB200020242007Burzić, ZijahGrabulov, VencislavSedmak, AleksanderSedmak, Stojanštevilka:44 straniletnik:41str. 163-166ISSN:1580-2949COBISSID:616874URN:URN:NBN:SI:doc-FYRMMQIKslInštitut za kovinske materiale in tehnologijeMateriali in tehnologijepreiskava materialarazpokeutrujenost materialovvisokotrdna jeklazvarjeni spojiFatigue properties of a high-strength-steel welded joint| Utrujenostne lastnosti zvara visokotrdnega jekla|In addition to the strength and toughness properties, the fatigue properties of welded joints are necessary for the design of high-strength steel structures exposed to variable loading. Wöhler curves were determined for smooth tensile specimens tested with variable loading. The fatigue behaviour of a welded joint can be improved by removing the overfill; however, the fatigue properties are still lower than the values for the parent metal. Tests with pre-cracked specimens have shown the difference in the fatigue-crack growth-rate properties to be less significant than other crack parametersUtrujenostne lastnosti so potrebne poleg trdnosti in žilavosti za načrtovanje struktur iz visokotrdnih jekel, ki prenašajo spremenljivo obremenitev. Wöhlerjeve krivulje so bile določene za gladke preizkušance in spremenljivo obremenitev. Utrujenostno vedenje zvarjenega spoja se lahko izboljša z odstranitvijo nadvišenja, vendar ostanejo utrujenostne lastnosti nižje kot pri osnovnem materialu. Preizkusi na vzorcih z razpoko so pokazali, da je manj izrazita razlika v hitrosti rasti razpoke kot pri drugih parametrih razpokeTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije