1529 KB25 KB200020242013Godec, MatjažJenko, MonikaSkobir Balantič, Danijela AnicaSteiner Petrovič, DarjaVodopivec, FrancŽužek, Borutletnik:47številka:6str. 819-824COBISSID:1010858ISSN:1580-2949URN:URN:NBN:SI:doc-BDLNTWGSenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijejeklalezenjemikrostrukturaStationary-creep-rate equations for tempered martensite| Enačbe za hitrost stacionarnega lezenja žarjenega martenzita|The stationary-creep equations including parameters as the average particle spacing or/and particle size are examined in terms of the effects of differentequation parameters on the difference of calculated and experimental creep rate. It is concluded that the difference between the experimental creeprate and the creep rate deduced from the recently proposed creep equationis in the range of about +-25 % if the effects of the steel compositionand the changes in the particle size and spacing during the creep test are considered with sufficient accuracyEnačbe za izračun hitrosti stacionarnega lezenja, ki vključujejo kot parametre povprečno velikost in oddaljenost izločkov, so analizirane s stališča razlike med eksperimentalno in izračunano hitrostjo lezenja. Sklep je: pred kratkim predložena enačba da razliko v razponu okoli 25 %, če so prav upoštevani vplivi sestave jekla in spremembe velikosti in oddaljenosti izločkov pri preizkusih lezenjaTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije