3323 KB0 KB200020242009Jeulin, DominiqueMorard, VincentMoreaud, MaximeRevel, Renaudletnik:28številka:37 stranistr. 187-193ISSN:1580-3139COBISSID:26424537URN:URN:NBN:SI:doc-B00QCZXJenDruštvo za stereologijo in kvantitativno analizo slike, Medicinska fakultetaImage analysis and stereologymaterialimikroskopijananodelciobdelava slikvelikost delcevSize of boehmite nanoparticles by TEM images analysis|Transition aluminas, and especially the gamma type, are largely used as catalyst supports in refining and petrochemicals. Most studies focus on properties resulting from material texture and casting (specific surface, porous volume, pore shape and diameter). However, surface properties of alumina should be considered as well, as the catalytic activity is tightly related to the structure of exposed crystalline faces. As y alumina results from controlled thermal treatment of boehmite y-AlOOH by a topotactic transformation, the nature of exposed crystalline planes is related to the starting material. Therefore, the synthesis of the oxihydroxide gamma-A1OOH, and especially size and shape of these particles, is critical in determining the relevant surface properties. Unlike often aggregated alumina, boehmite nanoparticles can be observed by TEM. Analysis of these TEM images can be performed to esrimate the size of the boehmite nanoparticles. Information about morphology of the nanoparticles is obtained by the analysis of the covariance, modeling micrographs by a dilution modelTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaDruštvo za stereologijo in kvantitativno analizo slike