43 KB759 KB28 KB200020242013Çetinarslan, Cem S.Güzey, Alištevilka:2letnik:47str. 245-252ISSN:1580-2949COBISSID:981162URN:URN:NBN:SI:doc-ARYEEUGGenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijedeformacijedeformationdrawing velocityhitrost vlečenjanatezne lastnostitensile propertiesvlečenje žicewire drawingTensile properties of cold-drawn low-carbon steel wires under different process parameters| Natezne lastnosti hladno vlečene maloogljične jeklene žice pri različnih parametrih procesa|This study demonstrates the influence of drawing-process parameters such as reduction (deformation) ratio and drawing velocity on the tensile properties of various low-carbon cold-malleable steel wires. Standard tensile tests were realized on four types of wires - SAE1006, SAE1008, SAE1015 (Cq15) and SAE10B22 (20MnB4) - at various process parameters. This experimental study shows how two of the main process parameters, the deformation ratio and drawing velocity, clearly influence the tensile properties (yield stress, ultimate tensile strength, and elongation at rupture) of steel-wire materialsTa študija prikazuje vpliv procesnih parametrov pri vlečenju, kot sta odvzem (deformacija) in hitrost vlečenja, na natezne lastnosti različnih maloogljičnih mehkih jeklenih žic. Izvršen je bil standardni natezni preizkus na štirih vrstah žice SAE1006, SAE1008, SAE1015 (Cq15) in SAE10B22 (20MnB4) po različnih procesnih parametrih. Ta eksperimentalna študija je pokazala, kako dva glavna procesna parametra, stopnja deformacije in hitrost vlečenja, vplivata na natezne lastnosti (napetost tečenja, natezna trdnost in raztezek pri pretrgu) jeklene žiceTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije