20 KB135 KB19 KB200020242001Bratina, GvidoBrownell, John NimlyHudej, RobertZavrtanik, Markoštevilka:3/4letnik:355 stranistr. 151-155ISSN:1580-2949COBISSID:172283URN:URN:NBN:SI:doc-9KUT5LJBenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijefotoprevodnostorganski polprevodniktanke plastiElectrical conductivity in 3,4,9,10-perylenetetracarboxylic dianhidride (PTCDA)| Električna prevodnost v 3,4,9,10 perilendianhidrid tetrakarboksilni kislini (PTCDA)|The transient photoresponse in 3,4,9,10-perylenetetracarboxylic dianhydride was examined in metal/organic semiconductor/metal heterostructures. Electron-hole pairs are generated within the structure for fields higher than 5 X 10sup4 V/cm as a consequence of the exciton dissociation. The mobility of the electrons perpendicular to the molecular layers increases with the applied electric field and saturates for fields higher than 5 X 10sup4 V/cmPreučevali smo tranzientno fotoprevodnost v tankih plasteh organskega polprevodnika 3,4,9,10-perilendianhidrida tetrakarboksilne kisline. V plasti polprevodnika nastanejo pari elektron-vrzel z disociacijo eksitonov pri jakosti električnega polja nad 5 X 10sup4 V/cm. Gibljivost elektronov pravokotno na molekularne plasti narašča z jakostjo električnega polja in doseže nasičenje pri jakosti 5 X 10sup V/cmTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije