20 KB364 KB19 KB200020242001Godec, MatjažJenko, MonikaMandrino, DjordjePrešern, Vasilijletnik:355 straništevilka:6str. 331-335ISSN:1580-2949COBISSID:327775URN:URN:NBN:SI:doc-2RXLCB4PenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijeAESatomizirani prahoviborkompozitioksidne plastisilicijželezoHR AES and XPS investigations of Fe-Si-B powders| HR AES- in XPS-preiskave prahov Fe-Si-B|Fe-Si-B powders for soft-magnetic composite (SMC) materials were prepared by water-atomisation. The as-prepared powders were analysed using high-resolution Auger-electron Spectroscopy (HR AES). The powders were heat treated in a dry or wet hydrogen. X-ray photoelectron spectroscopy (XPS) was then used to analyse the ion-etched surfaces of untreated and heat-treated Fe-Si-B powders that were sputtered for times from 0 to 1200 sZ vodno atomizacijo smo pripravili prahove Fe-Si-B za mehkomagnetne kompozite (SMC). Sveže pripravljene prahove smo analizirali z visokoločljivo spektroskopijo Augerjevih elektronov (HR AES). Prahove smo toplotno obdelali v suhem ali vlažnem vodiku. Nato smo z rentgensko fotoelektronsko spektroskopijo (XPS) analizirali ionsko jedkane površine neobdelanih in toplotno obdelanih prahov pri jedkalnih časih od 0 do 1200 s. Ugotovili smo, da so glavni konstituenti oksidnih plasti na zrnih prahov ?$\Fe_2SiO{4}$?, ?$\B_2O{3}? in ?$\SiO_2$?, da pa je njihova podrobna sestava močno odvisna od obdelave vzorca in globineTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije