48 KB514 KB33 KB200020242008Getsov, LeonidSemenov, ArtemStaroselsky, Alexanderštevilka:1letnik:42str. 3-12ISSN:1580-2949COBISSID:686250URN:URN:NBN:SI:doc-0N2BZEWRenInštitut za kovinske materiale in tehnologijeMateriali in tehnologijekovinemerjenjemetodemonokristaliobremenitvetrdnostutrujenostA failure criterion for single-crystal superalloys during thermocyclic loading| Merilo za prelom monokristala superzlitine pri termociklični obremenitvi|The accumulation of deformation affects the lifetime of a monocristal submitted to low cyclic mechanical and thermal loading. An analytical method was developed considering the damages due to cyclic and axial plastic and creep deformation. The method was checked with tests in vacuum on specimens of monocrystals with different space orientation, also specimens with stress concentrators. The distribution of stresses was FEM modelled. The fracture depends on the space orientation of the specimen and of the loading parameters. A new experimental-computational method using deformation-fracturecriteria is suggested for the evaluation of the crystal life timeKopičenje deformacije vpliva na trajnostno dobo kovine, ki prenaša malocklično mehansko in termično obremenitev. Razvita je bila analitična metoda, ki sešteva poškodbe zaradi cikličnih in enoosnih plastičnih deformacij in deformacije z lezenjem. Metoda je preverjena s preizkusi v vakuumu na vzorcih monokristalov z različno prostorsko orientacijo. Preizkusi so bili izvršeni tudi z vzorci z obliko, ki je povzročala lokalno koncentracijo napetosti. Porazdelitev napetosti je bila modelirana po metodi končnih elementov. Prelom je odvisen od prostorske orientacije in od parametrov obremenitve. Predlagana so nova deformacijsko-prelom na merila za oceno trajnostne dobe monokristala na podlagi eksperimentalno-računske analizeTEXTznanstveno časopisjejournalsSlovenian National E-content AggregatorNational and University Library of SloveniaInštitut za kovinske materiale in tehnologije