1172 Acta Chim. Slov. 2020, 67, 1172–1179 Vasić et al.: Epoxy functionalized carboxymethyl ... DOI: 10.17344/acsi.2020.6065 Scientific paper Epoxy Functionalized Carboxymethyl Dextran Magnetic Nanoparticles for Immobilization of Alcohol Dehydrogenase Katja Vasić,1 Željko Knez,1,2 Sanjay Kumar,3 Jitendra K. Pandey4 and Maja Leitgeb1,2* 1 University of Maribor, Faculty of Chemistry and Chemical Engineering, Smetanova 17, SI-2000 Maribor, Slovenia, phone: +386 2 2294 462, e-mail: maja.leitgeb@um.si 2 University of Maribor, Faculty of Medicine, Taborska ulica 8, SI-2000 Maribor, Slovenia 3 University of Petroleum and Energy Studies, Department of Chemistry, Dehradun, Uttarakhand, India 4 University of Petroleum and Energy Studies, Research and Developments, Dehradun, Uttarakhand, India * Corresponding author: E-mail: maja.leitgeb@um.si Received: 04-25-2020 Abstract Microbial inhibition of carboxymethyl dextran (CMD) magnetic nanoparticles (MNPs) was investigated on two different bacterial cultures, Escherichia coli and Staphylococcus aureus, where inhibition properties of CMD-MNPs were con- firmed, while uncoated MNPs exhibited no inhibition properties. To such CMD-MNPs, enzyme alcohol dehydrogenase (ADH) from Saccharomyces cerevisiae was immobilized. Later on, CMD-MNPs were functionalized, using an epoxide cross-linker epiclorohydrin (EClH) for another option of ADH immobilization. Residual activities of immobilized ADH onto epoxy functionalized and non-functionalized CMD-MNPs were determined. Effect of cross-linker concentration, temperature of immobilization and enzyme concentration on residual activities of immobilized ADH were determined, as well. With optimal process conditions (4% (v/v) EClH, 4 °C and 0.02 mg/mL of ADH), residual activity of immobi- lized ADH was 90%. Such immobilized ADH was characterized using FT-IR, SEM and DLS analysis. Keywords: Alcohol dehydrogenase, carboxymethyl dextran, epoxy functionalization, epichlorohydrin, enzyme activity 1. Introduction As versatile and efficient enzyme, alcohol dehydro- genases (ADH) has always had an important role in mod- ern green chemistry, especially since it can perform selec- tive oxidations and reductions.1,2 ADHs have many applications in production of various intermediates in chemical industries, such as production of chiral com- pounds, regeneration of different cofactors and in biosen- sors.3-6 However, poor stability presents a limitation in the industrial use of ADH and many strategies have been de- veloped to improve and increase its stability. These meth- ods include protein engineering, chemical modification and most commonly used immobilization.7–11 Iron oxide nanoparticles are often used as nanocarri- ers for enzyme immobilization and present a promising tool in various medical fields, which has numerous clinical applications, such as targeted drug delivery, cell labelling, tissue repairment and various applications in biosen- sors.12–16 Magnetic nanoparticles (MNPs) have unique properties, such as superparamagnetism, large surface area and low toxicity.17–19 However, they are inclined to aggre- gate, because of their strong magnetic dipole.20,21 To avoid such aggregation, modification of nanoparticles is in place. In our study, we used organic polymer carboxymethyl dex- tran (CMD) to provide better biocompatibility and biode- gradability with low toxicity of synthesized MNPs.22–25 Modified MNPs are usually further functionalized using different functionalization groups. Epoxy functional group is a very active group, which can react with proteins, enzymes and nucleic acids, resulting in beneficial immobi- lization of biomolecules. Epoxy groups are also very stable 1173Acta Chim. Slov. 2020, 67, 1172–1179 Vasić et al.: Epoxy functionalized carboxymethyl ... at neutral pH values, therefore different commercial sup- ports can be prepared at a far position, where the enzyme has to be immobilized, which means epoxy-activated sup- ports are very suitable biological systems to develop easy enzyme immobilization protocols.26,27 EClH is an epoxide with bifunctional alkylating activity and is routinely used in the production of numerous synthetic materials, includ- ing epoxy, phenoxy and polyamide resins, cross-linked starch, surfactants and many pharmaceutical products.28 There are studies describing epoxy-functionalized nano- particles, modified with silica, as a carrier for immobiliza- tion of ADH from horse liver to be a suitable support for immobilization of ADH,29,30 and studies reporting of im- mobilization of lipase and laccase covalently immobilized on magnetic microspheres, silica nanoparticles or chitosan magnetic beads via active epoxy groups.31–33 All reported studies show the importance and significance of ep- oxy-functionalized nanoparticles, suitable for enzyme im- mobilization. As there are many research studies investigating im- mobilization of ADH onto different magnetic supports, there are none that report about immobilization of ADH onto functionalized CMD-MNPs, using epichlorohydrin as an epoxide cross-linker. In our study, effect of process parameters was investigated, such as cross-linker concen- tration, temperature of immobilization and enzyme con- centration to obtain the highest residual activity of immo- bilized ADH. Additionally, characterization of such immobilized ADH was performed using FT-IR, SEM and DLS analysis. 2. Materials and Methods 2. 1. Materials CMD sodium salt, sodium phosphate, sodium pyro- phosphate, EClH (1-Chloro-2,3-epoxypropane), ethanol, β-nicotinamide adenine dinucleotide (β-NAD) and ADH from S. cerevisiae were purchased from Sigma-Aldrich. Iron (III) chloride hexahydrate (FeCl3 ∙ 6H2O), iron (II) chloride tetrahydrate (FeCl2 ∙ 4H2O), Coomassie brilliant blue, Peptone from meat, Meat extract, agar, Yeast extract and Tryptic soy broth were obtained from Merck. Ammo- nium hydroxide was purchased from Chem-Lab, Belgium. All reagents in this work were of analytical purity and used without further purification. In all experiments, deionized water was used. 2. 2. Methods 2. 2. 1. Synthesis and Toxicity of CMD-MNPs CMD-MNPs were prepared by protocol developed in our previous research, published by Vasić et al.34 Fur- ther we wanted to investigate the toxicity of the prepared CMD-MNPs. This was tested on two different bacterial cultures, Gram negative E. coli and Gram positive S. au- reus. Growth media for both bacterial cultures was pre- pared according to Table 1, later on sterilized and prepared as growth medium in a petri dish. E. coli and S. aureus with concentration of 105 CFU/mL were smeared on a petri dish, to which 10–30 mg of CMD-MNPs was added. Petri dishes with culture E. coli and S. aureus, together with CMD-MNPs, were incubated at 37 °C for 24 hours. 2. 2. 2. Immobilization of ADH Onto CMD-MNPs To CMD-MNPs, ADH and sodium acetate buffer (10 mM) were added with a volumetric ratio 1:9. Final ADH concentration in the reaction mixture was 0.02 mg/ mL. Immobilization was carried out for 2 hours at 4 °C and 22 °C, with 500 rpm. 2. 2. 3. Epoxy Functionalization of CMD-MNPs CMD-MNPs were functionalized with 4 % (v/v) EClH (0.5 M) in 10 mM sodium acetate buffer, pH 7.5. Functionalization was carried out with continuous mixing for 1 hour at 300 rpm and 22 °C. After functionalization, the supernatant was removed and epoxy functionalized CMD-MNPs were obtained. 2. 2. 4. Immobilization of ADH Onto Epoxy Functionalized CMD-MNPs To epoxy functionalized CMD-MNPs, ADH and so- dium acetate buffer (10 mM) were added with a volumet- ric ratio 1:9. Final ADH concentration in the reaction mix- ture was 0.02 mg/mL. Immobilization was carried out for 2 hours at 4 °C and 22 °C, with 500 rpm. 2. 2. 5. Assay for ADH Activity The activity of soluble and immobilized ADH was determined spectrophotometrically using ethanol as a substrate. The standard reaction mixture in a total volume of 3 mL contained 22 mM sodium pyrophosphate, 3.2% (v/v) ethanol, 7.5 mM β-NAD, 0.3 mM sodium phosphate and 0.003 (w/v) % BSA. The reaction was initiated by the addition of ethanol and β-NAD to soluble or immobilized ADH, and subsequently the increase in absorbance at 340 nm due to formation of β-NADH was measured. The activity of soluble and immobilized ADH was calculated using the following equation: Table 1. Growth media for E. coli and S. aureus E. coli S. aureus Peptone from meat 5 g Tryptic Soy Broth 30 g Meat extract 3 g Yeast extract 3 g Agar 15 g Agar 15 g Distilled H2O 1 L Distilled H2O 1 L 1174 Acta Chim. Slov. 2020, 67, 1172–1179 Vasić et al.: Epoxy functionalized carboxymethyl ... (1) where: 3 – total volume (mL) of assay df – dilution factor 6.22 – millimolar extinction coefficient of β-NADH at 340 nm 0.1 – volume (mL) of enzyme used Enzymatic activity of ADH was measured in tripli- cates by enzymatic assay for ADH by Sigma-Aldrich pro- tocol,35 and the residual activity was calculated from the following equation: (2) 2. 2. 6. Protein amount determination and immobilization efficiency calculation The protein amount of non-immobilized and immo- bilized ADH was determined by measuring the protein concentration by Bradford method using Bovine serum al- bumin (BSA) as a standard.36 The amount of ADH immobi- lized on the surface of CMD-MNPs was determined on the basis of the protein amount in supernatant fraction (cs) and later calculated by subtracting the measured amount (cs) from the amount of non-immobilized ADH (ce). Immobilization efficiency was calculated using the following equation: (3) where: cs – protein concentration in supernatant fraction of immobilized ADH ce – protein concentration of non-immobilized ADH All measurements for activity and protein amount determination were performed in triplicates and exhibited a standard deviation of less than 2%. 2. 3. Characterization 2. 3. 1. FT-IR FT-IR spectra were recorded to study chemical bonds formed between ADH immobilized CMD-MNPs. FT-IR analysis of the samples was performed by pressing the samples to form a tablet using KBr as the matrix. The spectra were detected over a range of 4000–500 cm–1 and recorded by a FT-IR spectrophotometer (Perkin Elmer 1600 Fourier transform infrared spectroscopy spectropho- tometer). 2. 3. 2. SEM The morphology and size of CMD-MNPs and ADH- CMD-MNPs was investigated by SEM analysis using a scanning electron microscope (FE, SEM SIRION, 400 NC, FEI). The samples were measured on a gold (Au) substrate. 2. 3. 3. DLS The particle size distribution, hydrodynamic size and ζ-potentials of the samples were measured using DLS (Zetasizer Nano ZS). Each diameter value was the average of three consecutive measurements. Higher values indicate a very broad size distribution, whereas lower values corre- spond to more or less monodisperse particle size distribu- tions. Measurements were carried out under equilibrium conditions. Measured samples were dispersed in water with neutral pH at room temperature. Concentration of all CMD-MNPs and ADH-CMD-MNPs were 2 mg/mL. 3. Results and Discussion 3. 1. Toxicity of CMD-MNPs Inhibition properties of synthesized CMD-MNPs on the growth of bacterial cultures E. coli and S. aureus were investigated, compared to uncoated magnetic nanoparti- cles. Qualitative assessment of inhibition properties was determined after incubation for 24 hours at 37 °C. If the Figure 1. Uncoated MNPs on bacterial culture E. coli after incuba- tion at 37 °C for 24 hours (a), CMD-MNPs on bacterial culture E. coli after incubation at 37 °C for 24 hours, where inhibition zone can be seen (b), uncoated MNPs on bacterial culture S. aureus after in- cubation at 37 °C for 24 hours (c) and CMD-MNPs on bacterial culture S. aureus after incubation at 37 °C for 24 hours, where inhi- bition zone can be seen (d). a) b) c) d) 1175Acta Chim. Slov. 2020, 67, 1172–1179 Vasić et al.: Epoxy functionalized carboxymethyl ... inhibition zone was present, additional quantitative as- sessment was performed. Figure 1 shows that inhibition occurs when CMD-MNPs were incubated with both bac- terial cultures, while uncoated MNPs exhibited no inhibi- tion properties. Additional quantitative assessment re- vealed that the average inhibition zone was 19.7 mm when incubated with E. coli and 19 mm, when incubated with S. aureus. CMD-MNPs exhibit antibacterial properties, since they are modified with organic polymer CMD. The modi- fication of MNPs with organic polymers makes MNPs bio- compatible, biodegradable and mostly non-toxic, which is a favourable advantage with using suitable support for im- mobilization of enzymes.17,18,37 3. 2. ADH Immobilization ADH was immobilized onto CMD-MNPs, which were not epoxy functionalized and onto epoxy functional- lized CMD-MNPs at two different immobilization tem- peratures, 4 °C and 22 °C. As seen from Figure 2a, residu- al activities increased drastically, when ADH was immobilized onto epoxy functionalized CMD-MNPs. Re- sidual activity at 22 °C increased from 15% to 39%, while at 4 °C it increased even more, from 26% to 87%. Results suggest that epoxy functionalized CMD-MNPs ensure more successful immobilization of ADH onto the surface of the carrier, since the functionalization of CMD-MNPs provides additional epoxy functional groups, to which the amino groups of the enzyme can bind. Further, we the influence of cross-linker concentra- tion on the residual ADH activity was studied. The con- centration of EClH was optimized by performing immobi- lization of ADH onto CMD-MNPs with different volumetric ratios of 0.5 M EClH as a cross-linking reagent. Enzyme residual activity was determined with the help of enzymatic assay for ADH determination, using ethanol as a substrate and immobilization efficiency was determined with the help of estimating the protein concentration with Bradford method in supernatants after immobilization and 2 times washing of the immobilized ADH-CMD- MNPs. As shown in Figure 2b, when applying 2% (v/v) of EClH, the residual activity was very low, only 19%, which could suggest that low cross-linker concentration gives poor mechanism strength, easily leading to leaching of the enzyme from carrier support. By doubling the concentra- tion of cross-linker EClH to 4% (v/v), the residual activity started to increase and was found to be optimal volumetric concentration, since it retained 88% of the original en- zyme activity. With increasing cross-linker concentration, the amount of free active groups on the surface of the car- rier resulted in higher ADH loading, causing higher resid- ual activity of immobilized ADH. Also, immobilization efficiency was very high, resulting in 100%. In this case, immobilization efficiency goes hand-in-hand with the re- sidual activity of ADH. With doubling the concentration of cross-linker EClH again, to 8% (v/v), residual activity and enzyme immobilization efficiency started to decrease. The significant residual activity decrease to 21% at 8% (v/v) of EClH suggests that the limit of cross-linking was reached. Too high concentration of cross-linker can result in enzyme deactivation on one hand and on the other hand the loss of activity happens because access concen- Figure 2. Residual activities of ADH immobilized onto CMD-MNPs, while investigating temperature of immobilization with and without epoxy functionalization (a) and cross-linker concentration (b). Table 1. Residual activities and immobilization efficiency of ADH immobilized onto epoxy functionalized CMD-MNPs, while investi- gating time of immobilization. Time of Residual Immobilization immobilization [h] activity [%] efficiency [%] 2 87 100 12 37 96 1176 Acta Chim. Slov. 2020, 67, 1172–1179 Vasić et al.: Epoxy functionalized carboxymethyl ... trations of cross-linker result in blocking of enzyme active groups.38 Immobilization efficiency was 89% for 8% (v/v) and 94% for 2% (v/v) of used EClH. The influence of immobilization time is presented in Table 1. At first, immobilization time was investigated at 2 hours, and later on prolonged to 12 hours. When perform- ing immobilization for 2 hours, residual activity of immo- bilized ADH-CMD-MNPs of 87% with 100% immobiliza- tion efficiency was achieved. When the immobilization time was prolonged to 12 hours, the residual activity of immobilized ADH-CMD-MNPs decreased drastically, to 37% with 96% immobilization efficiency. The results indi- cate that the immobilization time has an important effect on residual activity of immobilized ADH-CMD-MNPs and that the optimal immobilization lasts for 2 hours, which is sufficient time to bind enzyme ADH effectively to CMD-MNPS surface with its highest possible activity. substrate binding to form a product. When enzyme mole- cules crowd on the support surface, due to high enzyme concentration, enzyme molecules tend to overlap each oth- er. That overlapping leads to inaccessibility of enzyme mol- ecules’ active sites, therefore can not be bind with the sub- strate. As a consequence of this inaccessibility, the product can not be formed, which is expressed as reduced enzyme activity or denaturation of immobilized enzyme.39–42 3. 3. Characterization 3. 3. 1. FTIR, SEM, DLS Present peaks from FT-IR spectra of CMD-MNPs, ADH-CMD-MNPs and free ADH are presented in Table 3. ADH enzyme complex in ADH-CMD-MNPs shows char- acteristic absorption peaks at 1330 cm–1, 1640 cm–1 and 1450 cm–1 which can also be observed in the free ADH spectra, exhibiting characteristic frequencies of ADH com- plex at 1640 cm–1 and 1390 cm–1. The symmetric ring stretching frequency of the epoxy ring around 813, 921, and 1269 cm−1 were presented, indicating the existence of epoxy group on epoxy functionalized CMD-MNPs. The absorp- tion peaks at 569 cm–1 and 682 cm–1 belong to the stretch- ing vibration modes of Fe–O bond of synthesized MNPs. Characteristic adsorption peaks are shown at 1010 cm–1, which corresponds to CMD νC–O vibrations, while the broad absorption peak at 3408 cm–1 corresponds to the characteristic νO–H stretching and δO–H deformation modes of CMD hydroxyl groups, also CMD carboxyl groups are represented in absorption peak at 1642 cm–1. FT- IR spectra is available in Supplementary Material 1. The morphology of epoxy functionalized CMD- MNPs with immobilized ADH was investigated by SEM. Figure 3 shows SEM images of CMD-MNPs and epoxy functionalized ADH-CMD-MNPs. It is evident that CMD-MNPs and ADH-CMD-MNPs are spherical in shape and monodispersed. However, before immobiliza- tion of ADH, CMD-MNPs had more uniform size, which was in average 28 nm, as can be observed in our previous Table 2. Residual activities and immobilization efficiency of ADH immobilized onto epoxy functionalized CMD-MNPs, while investi- gating enzyme concentration. Enzyme concentration Residual Immobilization [mg/mL] activity [%] efficiency [%] 0.02 87 100 0.04 42 31 An increase in ADH concentration is suggested to yield in a more active product. However, with increase of enzyme concentration to 0.04 mg/mL the residual activity of immobilized ADH-CMD-MNPs decreased. When the ADH concentration was increased from 0.02 mg/mL to 0.04 mg/mL the residual activity decreased to 42% and im- mobilization efficiency decreased slightly more, to 31%. Re- sults can be observed in Table 2. The decrease in residual activity with increasing enzyme concentration can be at- tributed to the oversaturation of the enzyme over the sup- port surface. As enzyme has an active site, it is available for Table 3. Peaks from FT-IR spectra, present in soluble ADH, CMD-MNPs and ADH-CMD-MNPs. Wavenumber Functional Soluble CMD-MNPs ADH-CMD-MNPs [cm–1] group ADH 569 Fe-O x x 682 Fe-O x x 813 epoxy x x 921 epoxy x x 1010 νC–O x x 1269 epoxy x x 1330 ADH complex x x 1390 ADH complex x x 1450 ADH complex x x 1640 ADH complex x x 3408 νO–H, δO–H x x 1177Acta Chim. Slov. 2020, 67, 1172–1179 Vasić et al.: Epoxy functionalized carboxymethyl ... research.34 After immobilization CMD-MNPs are covered with a layer of enzyme due to epoxy functionalization, which allows ADH to covalently bind to CMD-MNPs. The sizes are slightly uneven and increased in diameter, rang- ing from 57 nm to 84 nm. Therefore, SEM images give ad- ditional evidence that ADH has been successfully bound to the surface of CMD-MNPs by covalent attachment re- sulting in the nano-sized product. Zeta potential of CMD-MNPs and ADH-CMD- MNPs was measured to indicate the stability of colloidal dispersion. Both prepared CMD-MNPs and immobilized ADH-CMD-MNPs exhibit negative zeta potentials, –31.9 mV and –26.8 mV, respectively, which indicate negatively charged hydroxyl and carboxyl groups of CMD present on the surface of nanoparticles. Zeta potentials indicate that CMD-MNPs and ADH-CMD-MNPs show good disper- sion in the aqueous phase. The size distribution of nanoparticles is expressed in polydispersity index (PdI). The PdI of ADH-CMD-MNPs is slightly higher, which is due to the layer of ADH, immobilized on the surface of CMD-MNPs, which can also be observed from SEM imag- es. Because ADH-CMD-MNPs are slightly uniform in size, the PdI index increases, as well. PdI values are pre- sented in Table 4. ture of immobilization and enzyme concentration were successfully optimized, resulting in 90% of residual activity of immobilized ADH. Characterization of immobilized ADH onto functionalized CMD-MNPs revealed successful covalent attachment and confirmed immobilization of ADH. The resulting CMD-MNPs with immobilized ADH were spherical in shape and measured from 57 nm to 84 nm in diameter. The results indicated that epoxy functionalized CMD-MNPs are favourable for ADH immobilization. Acknowledgment The authors acknowledge the financial support from the Slovenian Research Agency, research core funding Nr. P2-0046 – “Separation Processes and Product Design” and research core funding Nr. J2-1725 – “Smart materials for bioapplications”, “and grant INT/Slovenia/P-16/2014”. 6. References 1. de Smidt, O.; du Preez, J. C.; Albertyn, J. FEMS Yeast Res 2008, 8, 967–978. DOI:10.1111/j.1567-1364.2008.00387.x 2. Raj, S. B.; Ramaswamy, S.; Plapp, B. V. Biochemistry 2014, 53, 5791–5803. DOI:10.1021/bi5006442 3. Hummel, W.; Kula, M.-R. European Journal of Biochemistry 1989, 184, 1–13. DOI:10.1111/j.1432-1033.1989.tb14983.x 4. Alpat, S.; Telefoncu, A. Sensors (Basel) 2010, 10, 748–764. DOI:10.3390/s100100748 5. Patel, R. N. Coordination Chemistry Reviews 2008, 252, 659– 701. DOI:10.1016/j.ccr.2007.10.031 6. Demirkòran, N.; Ekinci, E. Acta Chim Slov 2012, 59, 302–306. 7. Bernal, C.; Rodríguez, K.; Martínez, R. Biotechnology Advanc- es 2018, 36, 1470–1480. DOI:10.1016/j.biotechadv.2018.06.002 8. Cowan, D. A.; Fernandez-Lafuente, R. Enzyme and Microbial Technology 2011, 49, 326–346. DOI:10.1016/j.enzmictec.2011.06.023 Figure 3. SEM images of CMD-MNPs (left) and ADH-CMD-MNPs (right). Table 4. Zeta-potential and PdI obtained by DLS analysis of CMD- MNPs and ADH-CMD-MNPs. Sample Sample Zeta-potential (mV) PdI CMD-MNPs –31.9 0.31 ADH-CMD-MNPs –26.8 0.53 4. Conclusions To conclude, CMD-MNPs were successfully func- tionalized with cross-linking of epoxide EClH for covalent attachment of ADH. Cross-linker concentration, tempera- 1178 Acta Chim. Slov. 2020, 67, 1172–1179 Vasić et al.: Epoxy functionalized carboxymethyl ... 9. Ahmad, R.; Sardar, M. Biochemistry & Analytical Biochemistry 2015, 0, 1–8. DOI:10.4172/2161-1009.1000178 10. Stojkovič, G.; Znidaršič-Plazl, P. Acta Chim Slov 2010, 57, 144–149. 11. Primožič, M.; Podrepšek, G.H.; Pavlovič, I.; Škerget, M.; Knez, Ž.; Leitgeb, M. Acta Chimica Slovenica 2019, 66, 732– 739. DOI:10.17344/acsi.2019.5013 12. Hola, K.; Markova, Z.; Zoppellaro, G.; Tucek, J.; Zboril, R. Biotechnology Advances 2015, 33, 1162–1176. DOI:10.1016/j.biotechadv.2015.02.003 13. Tarvirdipour, S.; Vasheghani-Farahani, E.; Soleimani, M.; Bardania, H. International Journal of Pharmaceutics 2016, 501, 331–341. DOI:10.1016/j.ijpharm.2016.02.012 14. Agiotis, L.; Theodorakos, I.; Samothrakitis, S.; Papazoglou, S.; Zergioti, I.; Raptis, Y.S. Journal of Magnetism and Magnetic Materials 2016, 401, 956–964. DOI:10.1016/j.jmmm.2015.10.111 15. Masood, F. Materials Science and Engineering: C 2016, 60, 569–578. DOI:10.1016/j.msec.2015.11.067 16. Kravanja, G.; Primožič, M.; Knez, Ž.; Leitgeb, M. Molecules 2019, 24, 1–23. DOI:10.3390/molecules24101960 17. Leitgeb, M.; Heržič, K.; Podrepšek, G.H.; Hojski, A.; Crnjac, A.; Knez, Z. Toxicity of magnetic chitosan micro and nan- oparticles as carriers for biologically active substances. Acta Chim Slov 2014, 61, 145–152. 18. Liu, G.; Gao, J.; Ai, H.; Chen, X. Small 2013, 9, 1533–1545. DOI:10.1002/smll.201201531 19. Markides, H.; Rotherham, M.; El Haj, A.J. Journal of Nanoma- terials 2012, 2012, 1–11. DOI:10.1155/2012/614094 20. Hauser, A.K.; Mathias, R.; Anderson, K.W.; Zach Hilt, J. Mate- rials Chemistry and Physics 2015, 160, 177–186. DOI:10.1016/j.matchemphys.2015.04.022 21. Wei, Y.; Han, B.; Hu, X.; Lin, Y.; Wang, X.; Deng, X. Procedia Engineering 2012, 27, 632–637. DOI:10.1016/j.proeng.2011.12.498 22. Agiotis, L.; Theodorakos, I.; Samothrakitis, S.; Papazoglou, S.; Zergioti, I.; Raptis, Y.S. Journal of Magnetism and Magnetic Materials 2016, 401, 956–964. DOI:10.1016/j.colsurfb.2012.10.030 23. Asmathunisha, N.; Kathiresan, K. Colloids and Surfaces B: Bi- ointerfaces 2013, 103, 283–287. DOI:10.1016/j.nano.2016.01.005 24. Alcantara, D.; Lopez, S.; García-Martin, M.L.; Pozo, D. Na- nomedicine: Nanotechnology, Biology and Medicine 2016, 12, 1253–1262. DOI:10.1016/j.taap.2010.08.029 25. Loh, J.W.; Yeoh, G.; Saunders, M.; Lim, L.-Y. Toxicology and Applied Pharmacology 2010, 249, 148–157. DOI:10.1021/bm0257661 26. Mateo, C.; Torres, R.; Fernández-Lorente, G.; Ortiz, C.; Fuentes, M.; Hidalgo, A.; López-Gallego, F.; Abian, O.; Pal- omo, J. M.; Betancor, L.; et al. Biomacromolecules 2003, 4, 772–777. DOI:10.2478/boca-2014-0001 27. Spinelli, D.; Coppi, S.; Basosi, R.; Pogni, R. Biocatalysis 2014, 1, 1–12. DOI:10.2478/boca-2014-0001. 28. National Toxicology Program Epichlorohydrin. Rep Carcinog 2011, 12, 180–183. DOI:10.1016/j.bbapap.2012.03.010 29. Petkova, G.A.; Záruba, K.; Král, V. Biochimica et Biophysica Acta (BBA) - Proteins and Proteomics 2012, 1824, 792–801. DOI:10.1016/j.ijbiomac.2016.03.031 30. Jiang, X.-P.; Lu, T.-T.; Liu, C.-H.; Ling, X.-M.; Zhuang, M.-Y.; Zhang, J.-X.; Zhang, Y.-W. Int. J. Biol. Macromol. 2016, 88, 9–17. DOI:10.1016/j.jmmm.2008.08.047 31. Lei, L.; Bai, Y.; Li, Y.; Yi, L.; Yang, Y.; Xia, C. Journal of Mag- netism and Magnetic Materials 2009, 321, 252–258. DOI:10.1016/j.bej.2015.04.020 32. Babaki, M.; Yousefi, M.; Habibi, Z.; Brask, J.; Mohammadi, M. Biochemical Engineering Journal 2015, 101, 23–31. DOI:10.1007/s00449-009-0345-6 33. Bayramoglu, G.; Yilmaz, M.; Yakup Arica, M. Bioprocess Bio- syst Eng 2010, 33, 439–448. DOI:10.1016/j.molcatb.2015.06.004 34. Vasić, K.; Knez, Ž.; Konstantinova, E.A.; Kokorin, A.I.; Gyer- gyek, S.; Leitgeb, M. Reactive and Functional Polymers 2020, 148, 1–13. DOI:10.1016/j.jbiotec.2006.01.028 35. Kägi, J.H.; Vallee, B.L. J. Biol. Chem. 1960, 235, 3188–3192. DOI:10.1016/j.jmmm.2010.08.008 36. Bradford, M.M. A rapid and sensitive method for the quanti- tation of microgram quantities of protein utilizing the princi- ple of protein-dye binding. Analytical Biochemistry 1976, 72, 248–254. DOI:10.1016/j.ijbiomac.2014.10.045 37. Bystrzejewska-Piotrowska, G.; Golimowski, J.; Urban, P.L. Waste Management 2009, 29, 2587–2595. DOI:10.1016/j.btre.2018.e00260 38. Chen, H.; Zhang, Q.; Dang, Y.; Guowei, S. Advanc Journal of Food Science and Technology 2013, 5, 932–935. DOI:10.1016/j.ijbiomac.2008.01.005 39. Jiang, D.-S.; Long, S.-Y.; Huang, J.; Xiao, H.-Y.; Zhou, J.-Y. Bi- ochemical Engineering Journal 2005, 25, 15–23. DOI:10.1016/j.procbio.2012.01.012 40. Prousoontorn, M.H.; Pantatan, S. J Incl Phenom Macrocycl Chem 2007, 57, 39–46. DOI:10.1016/j.reactfunctpolym.2020.104481 41. Talbert, J.N.; Goddard, J.M. Colloids and Surfaces B: Bioint- erfaces 2012, 93, 8–19. DOI:10.1016/j.colsurfb.2012.01.003. 42. Jamil, N.; Che Man, R.; Suhaimi, S.; Md Shaarani, S.; Iffah Mohd Arshad, Z.; Kholijah Abdul Mudalip, S.; Zubaidah Su- laiman, S. Materials Today: Proceedings 2018, 5, 22036–22042. DOI:10.1016/0003-2697(76)90527-3 1179Acta Chim. Slov. 2020, 67, 1172–1179 Vasić et al.: Epoxy functionalized carboxymethyl ... Except when otherwise noted, articles in this journal are published under the terms and conditions of the  Creative Commons Attribution 4.0 International License Povzetek Mikrobno inhibicijo magnetnih nanodelcev (MNP) prekritih z karboksimetil dekstranom (CMD) smo preučili na dveh bakterijskih kulturah, Escherichia coli in Staphylococcus aureus. Dokazali smo inhibicijske lastnosti CMD-MNP-jev, medtem ko neprekriti MNP-ji niso imeli te lastnosti. Na CMD-MNP smo imobilizirali alkohol dehidrogenazo (ADH) iz Saccharomyces cerevisiae. Poleg tega smo CMD-MNP-je funkcionalizirali z zamreževalcem epiklorhidrinom (EClH) kot alternativa za ADH imobilizacijo. Primerjali smo aktivnost ADH imobilizirane na epoksi funkcionalizirane CMD-MNP- je in nefunkcionalizirane. Pod optimalnimi pogoji priprave (4% (v/v) EClH, 4 °C in 0.02 mg/mL ADH) je imobilizirana ADH ohranila 90% aktivnosti. Tako imobilizirano ADH smo okarakterizirali z FT-IR, SEM in DLS.